Hot Corrosion Behavior of Hf-Doped NiAl Coating in the Mixed Salt of Na2SO4 + K2SO4 at 900 °C

被引：0

作者：

W. L. Zhang

W. Li

L. B. Fu

X. Peng

J. Sun

S. M. Jiang

J. Gong

C. Sun

机构：

[1] Chinese Academy of Sciences,Shi

[2] University of Science and Technology of China,Changxu Innovation Center for Advanced Materials, Institute of Metal Research

[3] Qilu University of Technology (Shandong Academy of Sciences),School of Materials Science and Engineering

来源：

Acta Metallurgica Sinica (English Letters) | 2023年 / 36卷

关键词：

Hot corrosion; Hafnium; Oxide scale; Titanium; Sulfide;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The hot corrosion behavior of the NiAl coating and the 5Hf-NiAl coating induced by mixed salt at 900 °C was investigated. Comparing with the NiAl coating, the 5Hf-NiAl coating exhibited superior hot corrosion resistance because the addition of Hf promoted the formation of protective oxide scale and reduced the growth rate of oxide scale. Therefore, internal sulfides were not present in the 5Hf-NiAl coating after hot corrosion for 140 h. Cr exhibited different distribution in the two coatings since the addition of Hf changed the hot corrosion process of the coating. Hf and Ti in the 5Hf-NiAl coating trapped and captured sulfur, preventing the penetration of sulfur into the coating. The hot corrosion mechanism of the two coating and the effects of Hf on this process were discussed in this work.

引用

页码：1409 / 1420

页数：11

共 50 条

[31] Influence of Pre-Oxidation on High Temperature Oxidation and Corrosion Behavior of Ni-Based Aluminide Coating in Na2SO4 Salt at 1050°C
Li, Qing
Zhang, Defeng
Song, Peng
Li, Zhenhua
Zhai, Ruixiong
Hua, Chen
Lu, Jiansheng
FRONTIERS IN MATERIALS, 2021, 8
[32] Hot Corrosion of Co-based Alloys with 25%NaCl+75%Na2SO4 Coating at 1173 K
Fu, Guangyan
Guo, Xingxing
Liu, Qun
Zhao, Xin
Su, Yong
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2013, 32 (03) : 317 - 321
[33] Study of hot corrosion resistance of electroless nickel coating with different content of phosphorous in molten salt deposit Na2SO4–NaCl at 650°C
Ghaderi M.
Rezagholizadeh M.
Nasiri-Vatan H.
Ebrahimi-Kahrizsangi R.
Surface Engineering and Applied Electrochemistry, 2015, 51 (04) : 367 - 373
[34] Corrosion of Fe-(10∼40)%Cr Steels in Na2SO4 Salts at 800∼900°C
Kim, Seul Ki
Lee, Jae Ho
Lee, Dong Bok
KOREAN JOURNAL OF METALS AND MATERIALS, 2012, 50 (05): : 361 - 368
[35] Hot Corrosion Behavior of Ni-Base Alloys Coated with Salt Film of 75%Na2SO4+25%NaCl at 900°C
Fu Guangyan
Qi Zeyan
Chen Jingyu
Liu Qun
Su Yong
RARE METAL MATERIALS AND ENGINEERING, 2015, 44 (05) : 1112 - 1115
[36] The effect of pre-oxidation on the hot corrosion behavior of CoNiCrAlHf alloy in Na2SO4 environment at elevated temperature
Ali, Rawaid
Song, Peng
Khan, Muhammad
Huang, Taihong
Ali, Shabir
Sha, Syed Hatim
Lu, Jiansheng
Ul Wahab, Zain
Pervaiz, Seemab
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2022, 128 (09):
[37] Hot Corrosion Behavior of ZrB2-SiC-Graphite Composite in NaCl and Na2SO4 Molten Salts
Liu, X.
Wang, G.
Liu, L.
Wang, Z.
Wu, Z.
Liu, M.
JOURNAL OF CERAMIC SCIENCE AND TECHNOLOGY, 2018, 9 (03): : 309 - 317
[38] Severe Hot Corrosion of the Superalloy IN718 in Mixed Salts of Na2SO4 and V2O5 at 700 °C
Dhananjay Pradhan
Girija Shankar Mahobia
Kausik Chattopadhyay
Vakil Singh
Journal of Materials Engineering and Performance, 2018, 27 : 4235 - 4243
[39] Severe Hot Corrosion of the Superalloy IN718 in Mixed Salts of Na2SO4 and V2O5 at 700 °C
Pradhan, Dhananjay
Mahobia, Girija Shankar
Chattopadhyay, Kausik
Singh, Vakil
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (08) : 4235 - 4243
[40] Hot-corrosion behavior of a La2Ce2O7/YSZ thermal barrier coating exposed to Na2SO4 + V2O5 or V2O5 salt at 900 °C
Wang, Xizhong
Guo, Lei
Peng, Hui
Zheng, Lei
Guo, Hongbo
Gong, Shengkai
CERAMICS INTERNATIONAL, 2015, 41 (05) : 6604 - 6609

← 1 2 3 4 5 →