Hot Corrosion Behavior of Hf-Doped NiAl Coating in the Mixed Salt of Na2SO4 + K2SO4 at 900 °C

被引：0
|
作者：
W. L. Zhang
W. Li
L. B. Fu
X. Peng
J. Sun
S. M. Jiang
J. Gong
C. Sun
机构：
[1] Chinese Academy of Sciences,Shi
[2] University of Science and Technology of China,Changxu Innovation Center for Advanced Materials, Institute of Metal Research
[3] Qilu University of Technology (Shandong Academy of Sciences),School of Materials Science and Engineering
来源：
Acta Metallurgica Sinica (English Letters) | 2023年 / 36卷
关键词：
Hot corrosion; Hafnium; Oxide scale; Titanium; Sulfide;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The hot corrosion behavior of the NiAl coating and the 5Hf-NiAl coating induced by mixed salt at 900 °C was investigated. Comparing with the NiAl coating, the 5Hf-NiAl coating exhibited superior hot corrosion resistance because the addition of Hf promoted the formation of protective oxide scale and reduced the growth rate of oxide scale. Therefore, internal sulfides were not present in the 5Hf-NiAl coating after hot corrosion for 140 h. Cr exhibited different distribution in the two coatings since the addition of Hf changed the hot corrosion process of the coating. Hf and Ti in the 5Hf-NiAl coating trapped and captured sulfur, preventing the penetration of sulfur into the coating. The hot corrosion mechanism of the two coating and the effects of Hf on this process were discussed in this work.
引用
收藏
页码：1409 / 1420
页数：11
相关论文
共 50 条
  • [21] Hot corrosion behavior of AlCuFeCr quasicrystalline coating on titanium alloy with the mixture of NaCl and Na2SO4 deposit
    Wang, Fengfeng
    Zhou, Chungen
    Gong, Shengkai
    Xu, Huibin
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 2313 - +
  • [22] Corrosion behavior of the NiCrAlY and NiSiAlY alloys with salt mixtures of NaCl/Na2SO4
    Zheng, Haiyang
    Cui, Tiancheng
    Zhu, Bing
    Yu, Xiaopeng
    Yu, Miao
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2024, 42 (02):
  • [23] Hot Corrosion Behavior of Inconel 625 in Na2SO4 and V2O5 Molten Salt System
    Li, Liang
    Li, Lanfeng
    Zhang, Guofeng
    Xue, Hongdi
    Cui, Maomao
    Wang, Wenxu
    Liu, Dexue
    METALS, 2023, 13 (06)
  • [24] Hot corrosion behavior and near-surface microstructure of a "low-temperature high-activity Cr-aluminide" coating on inconel 738LC exposed to Na2SO4, Na2SO4 + V2O5 and Na2SO4 + V2O5 + NaCl at 900 °C
    Doolabi, M. Salehi
    Ghasemi, B.
    Sadrnezhaad, S. K.
    Habibollahzadeh, A.
    Jafarzadeh, K.
    CORROSION SCIENCE, 2017, 128 : 42 - 53
  • [25] Comparison investigation of hot corrosion exposed to Na2SO4 salt and oxidation of MoSi2-based coating on Nb alloy at 1000 °C
    Sun, Le
    Fu, Qian-Gang
    Sun, Jia
    Zhang, Guang-peng
    SURFACE & COATINGS TECHNOLOGY, 2020, 385 (385)
  • [26] Influence of alloying elements on hot corrosion resistance of nickel-based single crystal superalloys coated with Na2SO4 salt at 900 °C
    Song, Peng
    Liu, Mingfeng
    Jiang, Xiangwei
    Feng, Yuchao
    Wu, Junjie
    Zhang, Gong
    Wang, Dong
    Dong, Jiasheng
    Chen, Xing-Qiu
    Lou, Langhong
    MATERIALS & DESIGN, 2021, 197
  • [27] Hot Corrosion Behavior of CM 247 LC Alloy in Na2SO4 and NaCl Environments
    I. Gurrappa
    Oxidation of Metals, 1999, 51 : 353 - 382
  • [28] Hot corrosion behavior of CM 247 LC alloy in Na2SO4 and NaCl environments
    Gurrappa, I
    OXIDATION OF METALS, 1999, 51 (5-6): : 353 - 382
  • [29] Na2SO4 Induced Hot Corrosion of Aluminized Low Carbon Steel at 700 °C
    Badaruddin, Mohammad
    ADVANCES IN APPLIED MECHANICS AND MATERIALS, 2014, 493 : 761 - 766
  • [30] Hot corrosion behavior of network structured TiBw/TA15 composite with Na2SO4 film at 800?C
    Kang, Qingxin
    Xu, Xiaoting
    Wang, Guofeng
    Luo, Shuyi
    Zhan, Liqiang
    MATERIALS CHARACTERIZATION, 2023, 195
12345