Analysis of the Solidification Process of Austenitic Stainless Steel Weld Metal using Synchrotron Radiation

被引:0
作者
Takahiro Osuki
Mitsuharu Yonemura
Kazuhiro Ogawa
Yu-ichi Komizo
Hidenori Terasaki
机构
[1] Sumitomo Metals Industries,R&D Laboratory
[2] Ltd.,Joining & Welding Research Institute
[3] Osaka University,undefined
来源
Welding in the World | 2009年 / 53卷
关键词
Austenitic stainless steels; Cracking; Defects; Hot cracking; Microstructure; Process conditions; Process parameters; Reference lists; Solidification cracking; Stainless steels; Steels; Speed; Simulating; Weld metal;
D O I
暂无
中图分类号
学科分类号
摘要
A numerical model to predict the solidification microstructure and solidification cracking susceptibility of austenitic stainless steel weld metals was proposed. It was predicted using the developed numerical model that Fe-20 %Cr-14.4 %Ni, Fe-20 %Cr-12.7 %Ni, Fe-20 %Cr-11.5 %Ni and Fe-20 %Cr-9.8 %Ni weld metals solidified as A mode (L→L + γ→γ), AF mode (L→L + γ→L + γ + δ→γ + δ), FA mode (L→L + δ→L + δ + γ→δ + γ) and FA mode, respectively. Also, it was found that the effect of Ni content on the solidification cracking susceptibility of Fe-20 %Cr-(9.8–14.4) %Ni weld metal, determined via trans-Varestraint testing, agreed with the results calculated using the model. In addition, in order to verify the validity of the developed numerical model, time-resolved in-situ observation of welding solidification process using synchrotron radiation has been carried out by changing the welding speed from 1 mm/s to 10 mm/s for Fe-20 %Cr-12.5 %Ni and Fe-20 %Cr-11.4 %Ni weld metals. It was found that the solidification mode of Fe-20 %Cr-12.5 %Ni weld metal transited from FA mode to AF mode by the higher welding speed and that of Fe-20 %Cr-11.4 %Ni weld metal maintained FA mode under the welding speed range of 1 mm/s to 10 mm/s. These results also coincided with the calculated results for Fe-20 %Cr-12.5 %Ni and Fe-20 %Cr-11.4 %Ni weld metals using the developed numerical model.
引用
收藏
页码:R290 / R303
相关论文
共 113 条
  • [1] Nishimoto K.(2001)Welding of stainless steel Tokyo, Japan, Sanpo 88 130-300s
  • [2] Natsume S.(1987)Effect of rapid solidification on stainless steel weld metal microstructures and its implication on the Schaeffler diagram Welding Journal 66 289s-76
  • [3] Ogawa K.(1979)Correlation between solidification cracking and microstructure in austenitic and austenitic-ferritic stainless steel welds Welding Research International 9 55-220
  • [4] Matsumoto O.(2003)Progress and future prospects of welding metallurgy JWS BULLETIN 15 219-38
  • [5] David S.A.(2003)Progress and future prospects of welding metallurgy JWS BULLETIN 15 27-139s
  • [6] Vitek J.M.(1994)Solidification behavior and cracking susceptibility of pulsed-laser welds in austenitic stainless steels Welding Journal 73 129s-238
  • [7] Hebble T.L.(1975)Kinetics of the diffusion controlled peritectic reaction during solidification of iron-carbon-alloys Metallurgical Transactions A 6A 235-859
  • [8] Kujanpåå V.P.(1986)Analysis of solute distribution in dendrites of carbon steel with δ/γ transformation during solidification Metallurgical Transactions B 17 845-210
  • [9] Suutala N.J.(1998)Finite difference simulation of peritectic transformation in iron-carbon alloy Materials Transactions JIM 39 203-552
  • [10] Takalo T.K.(1988)Numerical analysis of solute redistribution during solidification accompanying d/g transformation Transactions ISIJ 28 543-1321