Al/Fe isomorphic substitution versus Fe2O3 clusters formation in Fe-doped aluminosilicate nanotubes (imogolite)

被引:0
作者
Ehsan Shafia
Serena Esposito
Maela Manzoli
Mario Chiesa
Paola Tiberto
Gabriele Barrera
Gabriel Menard
Paolo Allia
Francesca S. Freyria
Edoardo Garrone
Barbara Bonelli
机构
[1] Politecnico di Torino,Department of Applied Science and Technology and INSTM Unit of Torino
[2] Università degli Studi di Cassino e del Lazio Meridionale,Politecnico
[3] Università di Torino,Department of Civil and Mechanical Engineering
[4] Electromagnetism,Dipartimento di Chimica and Centro Interdipartimentale NIS
[5] I.N.Ri.M.,Department of Chemistry and Chemical Biology
[6] Harvard University,Department of Chemistry
[7] Massachusetts Institute of Technology,undefined
来源
Journal of Nanoparticle Research | 2015年 / 17卷
关键词
Aluminosilicate nanotubes; Imogolite; Isomorphic substitution; High-spin Fe; sites; Fe; O; clusters; Paramagnetism; Band-gap; Nanocomposites;
D O I
暂无
中图分类号
学科分类号
摘要
Textural, magnetic and spectroscopic properties are reported of Fe-doped aluminosilicate nanotubes (NTs) of the imogolite type, IMO, with nominal composition (OH)3Al2−xFexO3SiOH (x = 0, 0.025, 0.050). Samples were obtained by either direct synthesis (Fe-0.025-IMO, Fe-0.050-IMO) or post-synthesis loading (Fe-L-IMO). The Fe content was either 1.4 wt% (both Fe-0.050-IMO and Fe-L-IMO) or 0.7 wt% (Fe-0.025-IMO). Textural properties were characterized by High-Resolution Transmission Electron Microscopy, X-ray diffraction and N2 adsorption/desorption isotherms at 77 K. The presence of different iron species was studied by magnetic moment measurements and three spectroscopies: Mössbauer, UV–Vis and electron paramagnetic resonance, respectively. Fe3+/Al3+ isomorphic substitution (IS) at octahedral sites at the external surface of NTs is the main process occurring by direct synthesis at low Fe loadings, giving rise to the formation of isolated high-spin Fe3+ sites. Higher loadings give rise, besides IS, to the formation of Fe2O3 clusters. IS occurs up to a limit of Al/Fe atomic ratio of ca. 60 (corresponding to x = 0.032). A fraction of the magnetism related to NCs is pinned by the surface anisotropy; also, clusters are magnetically interacting with each other. Post-synthesis loading leads to a system rather close to that obtained by direct synthesis, involving both IS and cluster formations. Slightly larger clusters than with direct synthesis samples, however, are formed. The occurrence of IS indicates a facile cleavage/sealing of Al–O–Al bonds: this opens the possibility to exchange Al3+ ions in pre-formed IMO NTs, a much simpler procedure compared with direct synthesis.
引用
收藏
相关论文
共 50 条
[21]   Transformation of a Fe–Mn oxide into a ferromagnetic α-Fe2O3 [J].
Apurva A. Narvekar ;
S. G. Tilve ;
J. B. Fernandes .
Journal of Thermal Analysis and Calorimetry, 2020, 142 :1207-1214
[22]   Adsorption of proteins on γ-Fe2O3 and γ-Fe2O3/SiO2 magnetic materials [J].
T. D. Khokhlova .
Russian Journal of Physical Chemistry A, 2017, 91 :2002-2006
[23]   Fe-doped Al2O3 nanoplatforms as efficient and recyclable photocatalyst for the dyes remediation [J].
Lerici, Laura C. ;
Leal Marchena, Candelaria ;
Torres, Cecilia C. ;
Campos, Cristian H. ;
Pierella, Liliana B. .
JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY, 2022, 426
[24]   Comparison between Fe2O3/C and Fe3C/Fe2O3/Fe/C Electrocatalysts for N2 Reduction in an Alkaline Electrolyte [J].
Kim, Ji Hye ;
Ju, HyungKuk ;
An, Byeong-Seon ;
An, Yena ;
Cho, Kanghee ;
Kim, Sun Hyung ;
Bae, Youn-Sang ;
Yoon, Hyung Chul .
ACS APPLIED MATERIALS & INTERFACES, 2021, 13 (51) :61316-61323
[25]   Fabrication and Formation Mechanism of Hollow-Structure Supermagnetic α-Fe2O3/Fe3O4 Heterogeneous Nanospindles [J].
Shaoshuai Zhang ;
Peng Deng ;
Lulu Yu ;
Yun Ni ;
Chen Ling ;
Ziye Zhu ;
Ruijiang Liu .
Journal of Inorganic and Organometallic Polymers and Materials, 2022, 32 :2492-2501
[26]   Selective synthesis of Fe3O4, γ-Fe2O3, and α-Fe2O3 using cellulose-based composites as precursors [J].
Liu, Shan ;
Yao, Ke ;
Fu, Lian-Hua ;
Ma, Ming-Guo .
RSC ADVANCES, 2016, 6 (03) :2135-2140
[27]   Fabrication and Characterization of Magnetic α-Fe2O3/Fe3O4 Heterogeneous Nanosheets [J].
Jie Wang ;
Min Liu ;
Yun Ni ;
Yao Yue ;
Mingyi Ma ;
Ruijiang Liu .
Journal of Inorganic and Organometallic Polymers and Materials, 2023, 33 :783-795
[28]   Influence of Fe2O3 on the structure and near-infrared emissivity of aluminosilicate glass coatings [J].
Abdelaziz Gahmousse ;
Kouider Ferria ;
Juan Rubio ;
Nilo Cornejo ;
Aitana Tamayo .
Applied Physics A, 2020, 126
[29]   Preparation of rGO, Fe2O3, and Fe2O3/rGO for the catalytic thermal decomposition of microspherical TKX-50 [J].
Huzeng Zong ;
Xiangdong Gao ;
Qiaoe Liu ;
Yanjun Hao ;
Gazi Hao ;
Suwei Wang ;
Hao Zhou ;
Lei Xiao ;
Wei Jiang .
Journal of Thermal Analysis and Calorimetry, 2022, 147 :12779-12790
[30]   A facile green approach of Fe2O3, Fe2O3 @Ag, Fe2O3 @AC and Fe2O3 @Ag@AC NPs synthesized via Cocos nucifera L for waste water treatment applications [J].
Mohan, N. S. ;
Gokulkumar, R. ;
Shankar, J. ;
Sridharan, R. ;
Logesh, B. ;
Sasikumar, R. ;
Vallarasu, K. ;
Vijayalakshmi, V. .
RESULTS IN CHEMISTRY, 2022, 4