Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 8. Effect of Firing Temperature on Properties of Materials Based on Mixed HCBS Composition: Bauxite, Quartz Glass, and Reactive Alumina1

被引：0
作者：
Yu. E. Pivinskii
P. V. Dyakin
A. Yu. Kolobov
机构：
[1] OOO NVF Kerambet-Ogneupor,
[2] FGBOU VPO St. Petersburg State Technological University (Technical University),undefined
[3] OAO Dinur,undefined
来源：
Refractories and Industrial Ceramics | 2017年 / 57卷
关键词：
HCBS; bauxite; reactive alumina; quartz glass; sintering; mullitization; non0isothermal heating; shrinkage; growth; ultimate strength in bending;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of firing temperature on shrinkage or growth indices, porosity, and ultimate strength in bending is studied in specimens prepared from bauxite HCBS, and also additionally containing reactive alumina CTC-30. For all material compositions there are typical preferred sintering temperature ranges (900 – 1200°C) with prevalent mullitization accompanied by an increase (1200 – 1400°C) in sintering or shrinkage of mullitized material (1400 – 1600°C).
引用
收藏
页码：637 / 644
页数：7
相关论文
共 31 条
  • [1] Pivinskii YE(2006)Pressure-molded high alumina ceramic castables. 3. Effect of processing additives on pressure — induced compaction and properties of bauxite-quartz glass matrix systems Refract. Indust. Ceram. 47 132-138
  • [2] Dyakin PV(2005)Pressure-molded high alumina ceramic castables. 1. Compaction and properties of matrix systems based on mixed HCBS of composition: bauxite, quartz glass, and commercial alumina Refract. Indust. Ceram. 46 220-224
  • [3] Dyakin PV(2005)Pressure-molded high-alumina ceramic castables. 2. Compaction and properties of materials based on plasticized bauxite HCBS, reactive alumina, find their binary mixtures Refract. Indust. Ceram. 46 396-402
  • [4] Pivinskii YE(1998)New refractory concretes and binding systems: Basic trends of development, production, and use of refractories in the 21st century. 2. Ceramic binders and castables Refract. Indust. Ceram. 39 91-99
  • [5] Dyakin PV(2015)Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 1. High-alumina bauxite as a basic raw material component Refract. Indust. Ceram. 56 344-350
  • [6] Vikhman SV(2015)Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 2. Properties of starting components and castings based on composite composition HCBS. Study of the initial stage of sintering and mullitization Refract. Indust. Ceram. 56 544-550
  • [7] Dyakin PV(2015)Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 3. Effect of firing temperature on sintering and mullitization of materials prepared on the basis of composite HCBS Refract. Indust. Ceram. 56 648-655
  • [8] Pivinskii YE(2016)Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 4. Effect of refractory clay addition on properties of compound composition HCBS, castings and materials based on them Refract. Indust. Ceram. 57 70-76
  • [9] Dyakin PV(2016)Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 5. Effect of firing temperature on properties of materials prepared from composite HCBS with addition of refractory clay Refract. Indust. Ceram. 57 180-184
  • [10] Vichman SV(2016)Research in the field of preparing molded and unmolded refractories based on high-alumina HCBS. Part 6. Mullitization and thermal expansion of materials based on compound composition HCBS Refract. Indust. Ceram. 57 297-303
1234