Effects of nanoclay on the thermal and rheological properties of a vartm (vacuum assisted resin transfer molding) epoxy resin

被引：0
作者：
Roberta Peila
J. C. Seferis
T. Karaki
G. Parker
机构：
[1] Polytechnic of Turin-Chemical Engineering Department,
[2] Glocal Network Corporation,undefined
[3] Toray Industries Inc.,undefined
[4] The Boeing Company,undefined
来源：
Journal of Thermal Analysis and Calorimetry | 2009年 / 96卷
关键词：
epoxy resin; nanocomposites; organo-montmorillonites; thermal stability; VARTM; viscosity;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Three types of commercially available organophilic Montmorillonite (Cloisite 30B, 25A and 15A) were used to prepare VARTM epoxy resin nanocomposites in order to study the effect of the nanoclay organophilic modification on the epoxy matrix. The morphology of the dispersions was investigated through XRD and TEM analyses. The thermal stability of the nanocomposites was studied by means of HI-RES TG measurements and the influence of the nanoclay on the viscosity of the resin was investigated through rheological measurements. It was found that the nanoclay modification had no significant influence on the dispersion and on the thermal properties of the nanocomposites. Areas of exfoliated and intercalated morphology were observed. The viscosity of the resin furthermore did not exceed the critical value of the infusion process.
引用
收藏
页码：587 / 592
页数：5
相关论文
共 84 条
  • [1] Gilbert E. N.(2001)undefined 33rd Int. SAMPE Tech. Conf., Seattle, WA 33 1368-undefined
  • [2] Hayes B. S.(2000)undefined 32nd SAMPE Tech Conf, Boston, MA, November 5–9 32 294-undefined
  • [3] Seferis J. C.(2003)undefined Polym. Comp. 2 672-undefined
  • [4] Hayes B. S.(2003)undefined Compos. Sci. Technol. 63 2201-undefined
  • [5] Gilbert E.N.(2001)undefined Polym. Comp. 22 477-undefined
  • [6] Seferis J. C.(2001)undefined Soc. Adv. Mat. Proc. Eng. (SAMPE) Tech. Conf., Seattle, WA, November 4–8 33 1379-undefined
  • [7] Moulton R.(2000)undefined Polym. Clay Nanocomp. 7 127-undefined
  • [8] Dixon D.(2004)undefined Compos. Sci. Techol. 64 2317-undefined
  • [9] Dai J.(2003)undefined Polym. Degrad. Stab. 80 383-undefined
  • [10] Pellaton D.(2004)undefined Polym. Eng. Sci. 44 345-undefined
123456789