Effects of mixed-mode overloading on the mixed-mode I+II fatigue crack growth

被引：0
|
作者：
Rahman Seifi
Mohammad Eshraghi
机构：
[1] Bu-Ali Sina University,Engineering Faculty
[2] Islamic Azad University,undefined
来源：
Archive of Applied Mechanics | 2013年 / 83卷
关键词：
Overloading; Mixed-mode I+II; Crack growth; Fatigue life; Residual stress;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, the finite element modeling of the compact tension shear specimens has been used to evaluate the effects of overloading on fatigue crack growth with mixed-mode loading I+II. Element creation and modeling is done by CASCA software. FRANC2D was used for stress analysis and the determination of crack parameters. Life estimation of samples was done by using the software ETBX. To create the mixed-mode I+II, different loading angles of 0, 15, 45 and 75 degrees (with respect to normal direction to the crack surface) were used with various overloading ratios. The effects of residual stresses due to overloading with saving and restoring capabilities were considered as a separate loading. To confirm the modeling results, models were built with ABAQUS and also compared with the results of numerical and experimental data in the literature. There are good agreements in determining the path of the crack growth and life estimation. The effects of the loading direction, overloading ratio and its load ratio, combination of overloadings and their locations on the fatigue crack growth and life are investigated.
引用
收藏
页码：987 / 1000
页数：13
相关论文
共 50 条
  • [41] Experimental characterization of cohesive zone models for thin adhesive layers loaded in mode I, mode II, and mixed-mode I/II by the use of a direct method
    Lelias, G.
    Paroissien, E.
    Lachaud, E.
    Morlier, J.
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2019, 158 : 90 - 115
  • [42] Three-dimensional finite element simulations of mixed-mode stable tearing crack growth experiments
    Lan, Weiming
    Deng, Xiaomin
    Sutton, Michael A.
    ENGINEERING FRACTURE MECHANICS, 2007, 74 (16) : 2498 - 2517
  • [43] STUDIES ON CYCLIC CRACK PATH AND THE MIXED-MODE CRACK CLOSURE BEHAVIOR IN AL-ALLOY
    MAGEED, AMA
    PANDEY, RK
    INTERNATIONAL JOURNAL OF FATIGUE, 1992, 14 (01) : 21 - 29
  • [44] Mixed-mode fracture in an R-curve material
    Gopalakrishnan, Karthik
    Mecholsky, John J., Jr.
    ENGINEERING FRACTURE MECHANICS, 2012, 79 : 380 - 388
  • [45] Analysis of fatigue crack growth under mixed-mode loading conditions for a pearlitic Grade 900A steel used in railway applications
    Nejad, Reza Masoudi
    Liu, Zhiliang
    ENGINEERING FRACTURE MECHANICS, 2021, 247
  • [46] Automatic mixed-mode crack propagation based on a combined hexahedral-tetrahedral approach
    Bremberg, D.
    Dhondt, G.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VI, 2007, 348-349 : 581 - +
  • [47] Mixed-Mode I-II Cracking Characterization of Mortar Using Phase-Field Method
    Hou, Yue
    Guo, Meng
    Ge, Zhi
    Sun, Wenjuan
    Wang, Linbing
    JOURNAL OF ENGINEERING MECHANICS, 2017, 143 (07)
  • [48] Estimating static/dynamic strength of notched unreinforced concrete under mixed-mode I/II loading
    Alanazi, N.
    Susmel, L.
    ENGINEERING FRACTURE MECHANICS, 2020, 240
  • [49] Mixed-mode fatigue failure criteria for adhesively-bonded pultruded GFRP joints
    Shahverdi, Moslem
    Vassilopoulos, Anastasios P.
    Keller, Thomas
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2013, 54 : 46 - 55
  • [50] Bilinear approximations to the mixed-mode I-II delamination cohesive law using an inverse method
    de Morais, A. B.
    Pereira, A. B.
    de Moura, M. F. S. F.
    Silva, F. G. A.
    Dourado, N.
    COMPOSITE STRUCTURES, 2015, 122 : 361 - 366
12345