Fluidized bed heat treatment of cast Al-Si-Cu-Mg alloys

被引:0
作者
S. K. Chaudhury
D. Apelian
机构
[1] the Metal Processing Institute (MPI),
[2] Worcester Polytechnic Institute (WPI),undefined
来源
Metallurgical and Materials Transactions A | 2006年 / 37卷
关键词
Material Transaction; Ultimate Tensile Strength; Solution Heat Treatment; Isopleth Diagram; Conventional Electrical Furnace;
D O I
暂无
中图分类号
学科分类号
摘要
The effects of fluidized bed heat treatment on the microstructural and mechanical properties of Al-Si-Cu-Mg cast alloys, namely, 354 and 319, were studied. The heating rate in fluidized beds (FBs) is greatervis-à-vis conventional electrical resistance furnaces (CFs). The high heating rate in FBs increases the kinetics of metallurgical phenomena such as Si fragmentation and spherodization during solution heat treatment, as well as the precipitation rate of phases such as Al5Cu2Mg8Si6 and Al2Cu during aging. It is observed that the dissolution rate of phases such as Mg2Si and Al5Cu2Mg8Si6 takes place very rapidly. The solution heat treatment of 319 alloy using FB results in complete dissolution of Mg2Si and Al5Cu2Mg8Si6 particles within 45 minutes. However, for phases such as Al2Cu and Ferich intermetallics, the dissolution rate is relatively slow. Even on prolonged solution heat treatment for 6 hours, these phases do not dissolve completely. It is observed that incomplete dissolution of the Al2Cu phase does not significantly affect tensile properties of T4-treated alloys. The optimum solution heat-treatment time in FB for both 354 and 319 alloys is 45 minutes at 527 °C and 493 °C, respectively. Thermal analysis shows an exothermic peak owing to recrystallization and coarsening of eutectic grains during solution heat treatment. The high heating rate in FB causes this transformation to take place at a lower temperature than in CF. It is observed that the nucleation rate of Al5Cu2Mg8Si6 during aging in FB is greater than using CF. Thermal analysis of samples during the ramp-up stage while aging using FB did not show any phase transformation, while those using CF show two endothermic transformations, which are most likely due to the dissolution of GP zones or the co-cluster of solutes. Aging at 200 °C results in a greater number density of precipitates than those at 240 °C. The tensile strength of samples aged at 200 °C is greater than those aged at 240 °C, because the amount of precipitates formed at 200 °C is greater than that at 240 °C. The total heat-treatment time for T6 temper is less than 2 hours in FBs, which is a significant reduction in heat-treatment time, as well as energy consumption.
引用
收藏
页码:2295 / 2311
页数:16
相关论文
共 91 条
[1]  
Apelian D.(1989)undefined AFS Trans. 89–137 727-41
[2]  
Shivkumar S.(1994)undefined Z. Metallkd. 85 394-99
[3]  
Sigworth G.(2004)undefined Mater. Sci. Eng., A 367 96-110
[4]  
Shivkumar S.(1995)undefined Metall. Mater. Trans. A 26A 2359-72
[5]  
Wang L.(2005)undefined Scripta Mater. 52 439-43
[6]  
Keller C.(1990)undefined AFS/SKANALUMINIUM 71 79-85
[7]  
Li Z.(2001)undefined J. Mater. Processing Technol. 109 174-80
[8]  
Samuel A.M.(2004)undefined Mater. Lett. 58 2096-101
[9]  
Samuel F.H.(1996)undefined Metall. Mater. Trans. A 27A 3983-991
[10]  
Ravindran C.(1990)undefined J. Mater. Sci. 25 2595-97