Growth and structures of C60 shells

被引：0

作者：

H. Sakuma

M. Tachibana

H. Sugiura

K. Kojima

S. Ito

T. Sekiguchi

Y. Achiba

机构：

[1] Yokohoma City University,Graduate School of Integrated Science

[2] Tohoku University,Research Institute for Materials

[3] Tokyo Metropolitan University,Department of Chemistry, Faculty of Science

来源：

Journal of Materials Research | 1997年 / 12卷

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The growth of the shells of C60 crystals was carried out under various conditions. The detailed structures of the grown shells were investigated by transmission electron microscopy and Raman spectroscopy. The shells were formed during thermal sublimation of the C60 crystals, which were irradiated with white light in air. The shells were mainly composed of a kind of amorphous carbon. From these results, it is suggested that the oxygen-induced disintegration of C60 cages is responsible for the shell formation.

引用

页码：1545 / 1550

页数：5

共 96 条

[1]

Haluska M(1993)undefined Appl. Phys. A 56 161-undefined

[2]

Kuzmany H(1994)undefined J. Cryst. Growth 143 58-undefined

[3]

Vybornnov M(1994)undefined Chem. Phys. Lett. 227 572-undefined

[4]

Rogl P(1994)undefined Chem. Phys. Lett. 217 413-undefined

[5]

Fejdi P(1995)undefined Thin Solid Films 257 185-undefined

[6]

Li J(1996)undefined J. Cryst. Growth 166 883-undefined

[7]

Mitsuki T(1992)undefined Solid State Commun. 84 827-undefined

[8]

Ozawa M(1992)undefined Appl. Phys. Lett. 60 2871-undefined

[9]

Horiuchi H(1980)undefined J. Non-Cryst. Solids 35&36 543-undefined

[10]

Kishio K(1982)undefined Phys. Rev. B 25 4142-undefined

← 1 2 3 4 5 6 7 8 9 10 →