On the Structural and Magnetic Properties of Mn-Bi Alloy Jet Milled at Different Feed Rates

被引:0
作者
V. V. Ramakrishna
S. Kavita
T. Ramesh
Ravi Gautam
R. Gopalan
机构
[1] International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI),Department of Mechanical Engineering
[2] National Institute of Technology,undefined
来源
Journal of Superconductivity and Novel Magnetism | 2021年 / 34卷
关键词
Rare-earth free permanent magnet; Mn-Bi; Jetmill; Magnetization; Coercivity;
D O I
暂无
中图分类号
学科分类号
摘要
Mn50Bi50 alloy was prepared using arc melting method with subsequent homogenization treatment. The homogenized alloy was crushed and subjected to jet mill at different feed rates. The weight fraction of the LTP MnBi phase determined by the Rietveld refinement of the XRD pattern was found to be 89% in the as-homogenized and crushed alloy. The crushed alloy was subjected to jet milling at different feed rates from 0.5 to 1.5 g/min. Structural studies show that increase in feed rate leads to phase decomposition. Magnetic studies show that as-homogenized crushed alloy exhibits a magnetization of 60 emu/g. Jet milling leads to increase in coercivity and a decrease in magnetization. However, it was found that increase in the feed rate during jet milling leads to decrease of both coercivity and magnetization. Microstructural studies show that jet milling leads to decrease in particle size. Jet milling done at a lower feed rate helps in yielding the lowest average particle size compared to remaining feed rates in the Mn-Bi alloy. The spin reorientation transition temperature of the Mn-Bi alloy decreases with jet milling and varies at different feed rates. The coercivity of the Mn-Bi powder jet milled with a lower feed rate increases from 14.7 kOe at room temperature to 19.4 kOe at 400 K.
引用
收藏
页码:733 / 737
页数:4
相关论文
共 132 条
  • [1] Guo X(1991)undefined J. Appl. Phys. 69 6067-83
  • [2] Altounian Z(1961)undefined J. Appl. Phys. 32 S201-undefined
  • [3] Stromolsen JO(1992)undefined Phys. Rev. B 46 14578-undefined
  • [4] Albert PA(2018)undefined Chin. Phys. B 27 117503-undefined
  • [5] Carr WJ(1974)undefined IEEE Trans. Magn. MAG-10 581-undefined
  • [6] Guo X(2013)undefined J. Phys. D. Appl. Phys. 46 062001-undefined
  • [7] Chena X(2014)undefined J. Magn. Magn. Mater. 349 9-undefined
  • [8] Altounian Z(2018)undefined J. Alloys and Comp. 744 432-undefined
  • [9] Stromolsen JO(2014)undefined J. Appl. Phys 115 17A756-undefined
  • [10] Yang J(1996)undefined J. Mater. Sci. Technol. 12 335-undefined