Microstructure and stresses in HVOF sprayed iron aluminide coatings

The microstructure and state of stress present in Fe3Al coatings produced by high velocity oxygen fuel (HVOF) thermal spraying in air at varying particle velocities were characterized using metallography, curvature measurements, x-ray analysis, and microhardness measurements. Sound coatings were produced for all conditions. The microstructures of coatings prepared at higher velocities showed fewer unmelted particles and a greater extent of deformation. Residual stresses in the coatings were compressive and varied from nearly zero at the lowest velocity to approximately −450 MPa at the highest velocity. X-ray line broadening analyses revealed a corresponding increase in the extent of cold work present in the coating, which was also reflected in increased microhardness. Values of mean coefficient of thermal expansion obtained for assprayed coatings using x-ray analysis were significantly lower than those for powder and bulk alloy.