One step preparation of highly dispersed TiO2 nanoparticles

被引：0
作者：
Xu Liu
Yan Chen
Shihui Jiao
Guangsheng Pang
机构：
[1] Jilin University,State Key Laboratory of Inorganic Synthesis and Preparative Chemistry, College of Chemistry
来源：
Chemical Research in Chinese Universities | 2015年 / 31卷
关键词：
TiO; nanoparticle; Water-dispersible; Colloid;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A facile approach was developed to prepare highly dispersed TiO2 nanoparticles with selected phase. The crystallization phase of the nanoparticles can be easily tuned from anatase to rutile by the dosage of hydrochloric acid in the reaction system. The crystallite size of the as-prepared anatase TiO2 nanoparticles was ca. 3.2 nm with high dispersion. A transparent TiO2 colloid was obtained by dispersing the as-prepared anatase TiO2 nanoparticles in deionized water without any organic additives added. The concentration of TiO2-H2O colloid can be as high as 1600 g/L. The optical transmittance of TiO2-H2O colloid with a low concentration was nearly 100% in the visible region. Furthermore, anatase TiO2 nanoparticles(TiO2-NPs) showed superior photocatalytic performance compared to rutile TiO2-NPs.
引用
收藏
页码：688 / 692
页数：4
相关论文
共 150 条
  • [1] Buso D.(2008)undefined Adv. Funct. Mater. 18 3843-undefined
  • [2] Post M.(2009)undefined Appl. Catal. A: Gen. 359 25-undefined
  • [3] Cantalini C.(2015)undefined J. Colloid Interface Sci. 456 161-undefined
  • [4] Mulvaney P.(2008)undefined Appl. Surf. Sci. 254 2685-undefined
  • [5] Martucci A.(2003)undefined J. Am. Chem. Soc. 125 9770-undefined
  • [6] Han F.(2007)undefined J. Am. Chem. Soc. 129 8406-undefined
  • [7] Kambala V. S. R.(2015)undefined Appl. Catal. B: Environ. 176 347-undefined
  • [8] Srinivasan M.(2005)undefined Angew. Chem. Int. Ed. 44 5115-undefined
  • [9] Rajarathnam D.(2012)undefined J. Mater. Chem. 22 7420-undefined
  • [10] Naidu R.(2005)undefined J. Am. Chem. Soc. 127 8659-undefined
12345678910