Effect of the annealing temperature on the long-range order in the B2 phase of the Ti-Al-Nb(Zr,Mo) alloy

被引：0

作者：

N. V. Kazantseva

V. A. Sazonova

G. A. Lyzhina

机构：

[1] Russian Academy of Sciences,Institute of Metal Physics, Ural Division

[2] Ural State Technical University (UGTU-UPI),undefined

来源：

The Physics of Metals and Metallography | 2006年 / 102卷

关键词：

61.66.Fn; 68.37.-d;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Investigation has been performed of changes in the degree of long-range order (LRO) upon annealing in a temperature range of 1000–1150°C for 1 h in the cubic B2 phase of the Ti-28.2% Al-13.2% Nb-1.2% Zr-0.86% Mo alloy. The calculation carried out using X-ray diffraction data showed that the degree of LRO in the B2 phase in the three-phase field (O + α2 + B2, T = 1000°C) is 0.36. Structure of the B2-phase regions with a low degree of LRO was studied using transmission electron microscopy. Temperature ranges suitable for thermomechanical treatment of the alloy have been determined.

引用

页码：288 / 294

页数：6

共 30 条

[1] Boehlert C. J.(2001)Part III. The Tensile Behavior of Ti-Al-Nb O + BCC Orthorhombic Alloys Metal. Trans. A 32A 1977-1988
[2] Banerjee D.(1988)A New Ordered Orthorhombic Phase in a Ti Acta Metall. 36 871-882
[3] Gogia A. K.(1989)Al-Nb Alloy Scr. Metall. 23 1697-1702
[4] Nandy T. K.(2000)Microstructures and Phase Relationships in the Ti Fiz. Met. Metalloved. 90 91-97
[5] Joshi V. A.(1970)Al-Nb System J. Appl. Crystallogr. 3 32-38
[6] Kestner-Weykamp H. I.(1987)Structural States of Ni Scr. Metall. 21 597-600
[7] Ward C. H.(1996)Al-Based intermetallic Compounds and Atomic Positions of Alloying Elements in Their Lattice Metall. Trans. A 27A 2593-2604
[8] Broderic T. F.(2001)Determination of the Order in the Intermetallic Phase Ni Acta Mater. 49 3971-3980
[9] Kaufman M. J.(2003)Al As a Function of Temperature Fiz. Met. Metalloved. 96 23-32
[10] Goman’kov V. I.(2005)Site Occupation in the Ordered Beta Phase of Ternary Ti-Al-Nb Alloys Deformat. Razrush. Mater. 1 34-39

← 1 2 3 →