The effects induced by proton irradiation on structural characteristics of nuclear graphite

被引：0
作者：
Mohammad Amin Amirkhani
Mohsen Asadi Asadabad
Mostafa Hassanzadeh
Seyed Mohammad Mirvakili
机构：
[1] Nuclear Science and Technology Research Institute,Reactor and Nuclear Safety Research School
来源：
Journal of Radioanalytical and Nuclear Chemistry | 2019年 / 321卷
关键词：
Proton irradiation; Nuclear graphite; X-ray diffraction; Raman spectroscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A grade TSX graphite was irradiated by a 2.5 MeV proton and a dose of 1.47 × 1018 ion cm−2 at 330 K. The displacement per atom under this irradiation condition was about 0.02. The lattice parameter, crystallite size and the vacancies density in the graphite was measured before and after irradiation. It was found that the proton irradiation led to an increase in the volume of the sample. The volume change in the irradiated sample was confirmed by atomic force and scanning electron microscopes observations as increased roughness and pore size. Also, FTIR results showed that graphite is slightly oxidized by irradiation.
引用
收藏
页码：701 / 709
页数：8
相关论文
共 154 条
[21]  
Djerourou W(2003)Proton irradiation emulation of PWR neutron damage microstructures in solution annealed 304 and cold-worked 316 stainless steels J Nucl Mater 323 18-333
[22]  
Medjkoun H(2002)Emulation of neutron irradiation effects with protons: validation of principle J Nucl Mater 300 198-564
[23]  
Nairy RK(2017)An understanding of lattice strain, defects and disorder in nuclear graphite Carbon 124 314-190
[24]  
Bhat NN(1993)X-ray diffraction, thermal expansion, electrical conductivity, and optical microscopy studies of coal-based graphites Carbon 31 557-261
[25]  
Anjaria K(1970)Graphitization of soft carbons Chem Phys Carbon 6 125-1509
[26]  
Sreedevi B(1951)The structure of graphitic carbons Acta Crystallogr A 4 253-31
[27]  
Sapra B(1954)X-ray study of the graphitization of carbon black J Appl Phys 25 1503-180
[28]  
Narayana Y(1953)X-ray line broadening from filed aluminium and wolfram Acta Metall 1 22-565
[29]  
Amirkhani MA(1998)The (hkl) dependence of diffraction-line broadening caused by strain and size for all Laue groups in Rietveld refinement J Appl Crystallogr 31 176-57
[30]  
Asadabad MA(2015)Neutron irradiation damage of nuclear graphite studied by high-resolution transmission electron microscopy and Raman spectroscopy J Nucl Mater 467 557-339
12345678910