Migration behavior and aggregation mechanism of SiC particles in silicon melt during directional solidification process

被引:0
作者
Yue Yang
Shi-qiang Ren
Da-chuan Jiang
Zhi-qiang Hu
Yi Tan
Peng-ting Li
机构
[1] Dalian University of Technology,School of Materials Science and Engineering
[2] Liaocheng University,School of Medicine
[3] Shanghai University,State Key Laboratory of Advanced Special Steel
来源
China Foundry | 2021年 / 18卷
关键词
polycrystalline silicon; SiC; directional solidification; migration; TG146; A;
D O I
暂无
中图分类号
学科分类号
摘要
SiC inclusions in a multicrystalline silicon ingot have a negative effect on the performance of solar cells. The migration behavior and aggregation mechanism of SiC particles in the silicon melt during the directional solidification process was studied. Results show that SiC particles collide and aggregate in the melt due to the effect of melt flow. Larger aggregation of SiC particles is easily deposited at the bottom of the melt, whereas smaller SiC particles are pushed to the top of melt. Meanwhile, the particles migrate to the edge of melt under the effect of electromagnetic force. Furthermore, the enrichment region of SiC particles can be controlled by adjusting the temperature field distribution of the melt. With an increase of the melt temperature, the SiC particles are enriched at the top of the silicon ingot, indicating that SiC particles can be effectively separated from silicon.
引用
收藏
页码:550 / 556
页数:6
相关论文
共 50 条
  • [31] Interactions between γ-TiAl melt and Y2O3 ceramic material during directional solidification process
    Cui Ren-jie
    Zhang Hua-rui
    Tang Xiao-xia
    Ma Li-min
    Zhang Hu
    Gong Sheng-kai
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2011, 21 (11) : 2415 - 2420
  • [32] Distribution Behavior of B and P during Al-Si Melt Directional Solidification with Open-Ended Crucible
    Bai, Xiaolong
    Ban, Boyuan
    Li, Jingwei
    Peng, Zhijian
    Chen, Jian
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (03) : 201 - 208
  • [33] Numerical study of melt flow under the influence of heater-generating magnetic field during directional solidification of silicon ingots
    Li, Zaoyang
    Qi, Xiaofang
    Liu, Lijun
    Zhou, Genshu
    JOURNAL OF CRYSTAL GROWTH, 2018, 484 : 78 - 85
  • [34] Effect of Pulling Rate on Multicrystalline Silicon Ingot during Directional Solidification
    Sun, Shihai
    Tan, Yi
    Zhang, Huixing
    Dong, Wei
    Zhang, Junshan
    Hu, Genxiong
    ADVANCED MATERIAL SCIENCE AND TECHNOLOGY, PTS 1 AND 2, 2011, 675-677 : 53 - 56
  • [35] Cellular Automaton Modeling of Silicon Facet Formation during Directional Solidification
    Wang, Jia
    Li, Ri
    Li, Ning
    Yan, Wenbo
    Ma, Wang
    Chen, Hongjian
    CRYSTALS, 2018, 8 (11)
  • [36] A model for distribution of iron impurity during silicon purification by directional solidification
    Wen, Shutao
    Tan, Yi
    Yuan, Tao
    Li, Pingting
    Forzan, Michele
    Jiang, Dachuan
    Dughiero, Fabrizio
    VACUUM, 2017, 145 : 251 - 257
  • [37] Dislocation Density Analyses of Multi-Crystalline Silicon During the Directional Solidification Process with Bottom Grooved Furnace
    Karuppasamy, P.
    Srinivasan, M.
    Aravinth, K.
    Ramasamy, P.
    DAE SOLID STATE PHYSICS SYMPOSIUM 2015, 2016, 1731
  • [39] Numerical simulation and experimental verification of vacuum directional solidification process for multicrystalline silicon
    Lv, Guoqiang
    Chen, Daotong
    Yang, Xi
    Ma, Wenhui
    Luo, Tao
    Wei, Kuixianai
    Zhou, Yang
    VACUUM, 2015, 116 : 96 - 103
  • [40] The carbon distribution in multicrystalline silicon ingots grown using the directional solidification process
    Teng, Ying-Yang
    Chen, Jyh-Chen
    Lu, Chung-Wei
    Chen, Chi-Yung
    JOURNAL OF CRYSTAL GROWTH, 2010, 312 (08) : 1282 - 1290