Effect of Non-metallic Inclusions in Fe-Al-Ti-O-N-S Alloy on Grain Size

被引:0
作者
Wonjin Choi
Hiroyuki Matsuura
Fumitaka Tsukihashi
机构
[1] The University of Tokyo,Department of Advanced Materials Science, Graduate School of Frontier Sciences
[2] Yonsei University,School of Advanced Material Engineering
来源
Metallurgical and Materials Transactions B | 2016年 / 47卷
关键词
Al2O3; Austenite; Heated Sample; Size Number; Ferritic Stainless Steel;
D O I
暂无
中图分类号
学科分类号
摘要
The effect of characteristics of non-metallic inclusions in Fe-Al-Ti-O-N-S alloys with various compositions at 1473 K (1200 °C) on the microstructure was studied. The ASTM grain size number was determined in as-cast and heated samples by the optical microscopy, and the inclusion types in each sample were determined from composition analysis by field-emission scanning electron microscope with energy-dispersive spectroscopy. The TiN-based inclusions certainly had a positive effect on the grain refinement. On the other hand, TiS-based inclusions exhibited no influence on the decrease of grain size. In addition, the formation and evolution behavior of inclusions by heating solid-state Fe-Al-Ti-O-N-S alloys with those locations were clarified. A different change of inclusions in alloys was observed depending on the distribution and composition of inclusions.
引用
收藏
页码:1851 / 1857
页数:6
相关论文
共 34 条
[1]  
Matsuda S.(1978)undefined Trans. ISIJ 18 198-205
[2]  
Okumura N.(2008)undefined ISIJ Int. 48 294-300
[3]  
Ohta H.(2007)undefined ISIJ Int. 47 1255-64
[4]  
Inoue R.(2001)undefined Tetsu-to-Hagane 87 707-12
[5]  
Suito H.(1996)undefined Mater. Trans. JIM 37 1554-60
[6]  
Kikuchi N.(2011)undefined ISIJ Int. 51 1951-56
[7]  
Nabeshima S.(2013)undefined ISIJ Int. 53 2007-12
[8]  
Kishimoto Y.(1996)undefined ISIJ Int. 36 1286-94
[9]  
Matsushita T.(2004)undefined ISIJ Int. 44 1016-23
[10]  
Sridhar S.(1974)undefined Metall. Trans. 5 2165-78