Preparation of superfine-cemented carbide by spark plasma sintering

被引：0

作者：

Xie Y. ^{[1
]}

Wang X. ^{[1
]}

Chen L. ^{[2
]}

Li X. ^{[1
]}

Guo H. ^{[1
]}

机构：

[1] School of Materials Science and Engineering, Shanghai University

[2] Shanghai Institute of Ceramics, Chinese Academy of Sciences

来源：

J Wuhan Univ Technol Mater Sci Ed | 2006年 / 1卷 / 42-45期

关键词：

Cemented carbide; Sintering mechanism; Spark plasma sintering; Superfine grain;

D O I：

10.1007/BF02861467

中图分类号：

学科分类号：

摘要：

92WC-8Co powder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering (SPS) and sintering isostatic pressure (SIP). Complete dense samples with 200 nm WC grains and 94.2HRA hardness were prepared by spark plasma sintering at 1150°C and under 4.5 kN for 5 minutes, SIP was carried out at 1400°C for 30 minutes with a result of 300-400 nm WC grains and 93 HRA hardness. The results show that sintering temperature is greatly decreased by SPS, sintering time is largely shortened and WC grain growth is effectively retarded. Micropores and drawbacks in superfine-cemented carbide made by SPS are greatly declined, which is very useful to improving mechanical properties.

引用

页码：42 / 45

页数：3

共 25 条

[1]

She Zhen-hui(1998)The Development of Sintering Technique of Cemented Carbide Cemented Carbide 15 49-53

[2]

Zhang Dong-ming(1999)Mechanism and Application of Spark Plasma Sintering Technology Journal of Wuhan University of Technology-Mater. Sci. Ed. 21 15-17

[3]

Fu Zheng-yi(2001)Current Progress of Materials Produced by Spark Plasma Sintering Powder Metallurgy Industry 11 7-16

[4]

Luo Xi-yu(2002)The Development and Application of Spark Plasma Sintering Powder Metallurgy Technology 20 129-134

[5]

Zhang Jiu-xing(2002)Equivalent Resistance in Pulse Electric Current Sintering Wuhan Univ. Tech.-Mat. Sci. Ed. 17 30-32

[6]

Liu Ke-gao(2001)Effect of Heating Rate on Spark Plasma Sintering TiB Chinese Journal of Materials Research 15 484-486

[7]

Zhang Dong-ming(2003) Ceramic Materials Science and Engineering A351 31-38

[8]

Fu Zheng-yi(2003)Spark Plasma Sintering Behavior of Superfinecrystalline WC-10Co Cemented Carbide Powders Wuhan Univ. Tech. -Mat. Sci. Ed. 18 82-84

[9]

Fu Zheng-yi(1999)Specific Property of Ultrafine Particle Classification Journal of Inorganic Materials 14 985-988

[10]

Pang Ting-ting(2001)Fabrication of Superfine 3Y-TZP by Spark Plasma Sintering Journal of Ceramics 22 157-160

← 1 2 3 →