Preparation of Nickel-Cobalt/Carborundum Carbide Composite Coatings by Supergravity Field-Enhanced Electrodeposition

被引:0
作者
Xiaoyun Hu
Ningsong Qu
机构
[1] Nanjing University of Aeronautics and Astronautics,
[2] Jiangsu Key Laboratory of Precision and Micro-Manufacturing Technology,undefined
来源
Chinese Journal of Mechanical Engineering | 2020年 / 33卷
关键词
Supergravity field; Electrodeposition; Microhardness; Wear resistance;
D O I
暂无
中图分类号
学科分类号
摘要
Nickel-cobalt/silicon carbide (Ni-Co/SiC) composite coatings were fabricated by supergravity field-enhanced electrodeposition. The surface morphology and the distribution of the SiC particles in the coatings were examined by scanning electron microscope and energy dispersive X-ray spectrometry. The preferred orientations of the coatings were measured by X-ray diffractometry. The wear resistance and microhardness were measured by a reciprocating tribometer and a microhardness instrument, respectively. The results revealed that the use of the supergravity field enhanced the smoothness of the as-deposited Ni-Co/SiC coatings, and the SiC nanoparticles were uniformly distributed in comparison with that for conventional electrodeposition. When the rotation speed of the cathode, which provided the supergravity field, was 800 r/min, the SiC content in the coating reached a maximum of 8.1 wt%, which was a much higher content than the 2.2 wt% value obtained under conventional electrodeposition. The highest coating microhardness of 680 HV was also observed at this rotation speed. In addition, the wear resistance of the as-prepared Ni-Co/SiC coatings exhibited improved performance relative to that prepared under normal gravity. A minimum wear weight loss of 1.4 mg together with an average friction coefficient of 0.13 were also realized at a rotation speed of 800 r/min, values which were much lower than those for normal gravity.
引用
收藏
相关论文
共 97 条
[1]  
Ignatova K(2017)Composition and structure of Ni-Co coating depending on the ratio of Ni and Co in a citrate electrolyte Bulgarian Chemical Communications 49 313-319
[2]  
Marcheva Y(2016)Hierarchical NiCo Advanced Functional Materials 26 4661-4672
[3]  
Sivanantham A(2017)S ACS Catalysis 7 4131-4137
[4]  
Ganesan P(2016) nanowire arrays supported on Ni foam: an efficient and durable bifunctional electrocatalyst for oxygen and hydrogen evolution reactions Engineering Science and Technology, An International Journal 19 1526-1533
[5]  
Shanmugam S(2019)Nest-like NiCoP for highly efficient overall water splitting Surface and Coatings Technology 372 463-498
[6]  
Du C(2016)Multi-objective optimization of electroless ternary Nickel–Cobalt–Phosphorous coating using non-dominant sorting genetic algorithm-II Journal of Laboratory Automation 21 394-401
[7]  
Yang L(2013)A review of electrodeposited Ni-Co alloy and composite coatings: Microstructure, properties and applications Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing 559 583-590
[8]  
Yang F(2015)Intelligent computation for optimal fabrication condition of a protein chip with Ni-Co alloy-coated surface Transactions of the IMF 93 275-280
[9]  
De J(2014)The effect of SDS surfactant on tensile properties of electrodeposited Ni–Co/SiC nanocomposites Surface and Coatings Technology 253 76-82
[10]  
Banerjee T(2018)The electrodeposition of nanocrystalline Cobalt-Nickel-Phosphorus alloy coatings: A review Ceramics International 44 6466-6473