Phase Equilibria in the Cu–Ti–Zr System at 750°C. I. The Isothermal Section with Copper Content from 0 to 50 at.%

被引：0
|
作者：
A. M. Storchak-Fedyuk
L. V. Artyukh
L. A. Duma
P. G. Agraval
M. A. Turchanin
T. Ya. Velikanova
机构：
[1] National Academy of Sciences of Ukraine,Frantsevich Institute for Problems of Materials Science
[2] Donbass State Mechanical Engineering Academy,undefined
来源：
Powder Metallurgy and Metal Ceramics | 2017年 / 56卷
关键词：
Cu–Ti–Zr system; isothermal section; lattice parameters;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Optical and scanning electron microscopy, electron microprobe analysis, and X-ray diffraction are employed to examine alloys in the Cu–Ti–Zr ternary system, annealed at 750°C, with copper content from 0 to 50 at.%. A partial isothermal section of the phase diagram is constructed at 750°C in the composition range in question. The existence of a continuous series of solid solutions between CuTi2 and CuZr2 isostructural compounds (γ phase, MoSi2 type) is confirmed. The homogeneity ranges of Cu2TiZr ternary compound (τ1, MgZn2 type) and β-(Ti, Zr), (CuTi) (CuTi type), and CuZr (CsCl type) solid solutions are determined.
引用
收藏
页码：78 / 87
页数：9
相关论文
共 41 条
  • [21] Phase Equilibria in the Ternary Al–Ti–Pt System. III. The Al–Ti–Pt Melting Diagram in the Composition Range 0–50 at.% Pt
    O. V. Zaikina
    V. G. Khoruzhaya
    K. Ye. Korniyenko
    T. Ya. Velikanova
    Powder Metallurgy and Metal Ceramics, 2019, 58 : 81 - 88
  • [22] Phase Equilibria in the Ternary Al–Ti–Pt System. IV. Vertical Sections in the Ternary Al–Ti–Pt System in the Composition Range 0–50 at.% Pt
    V. G. Khoruzhaya
    K. Ye. Korniyenko
    Powder Metallurgy and Metal Ceramics, 2019, 58 : 323 - 328
  • [23] The Co–Ni–Zr Phase Diagram in the Zr–ZrCo–ZrNi Region I. Phase Equilibria in the Zr–ZrCo–ZrNi System at Subsolidus Temperature, 900°C, and 800°C
    O.L. Semenova
    V.M. Petyukh
    O.S. Fomichov
    Powder Metallurgy and Metal Ceramics, 2021, 59 : 564 - 575
  • [24] Phase equilibria in the Ti-rich corner of the Ti-Si-Sn-Al system - Part I - Section 9Si-1Sn (at.%)
    Bulanova, M
    Soroka, A
    Zheltov, P
    Tretyachenko, L
    Meleshevich, K
    Samelyuk, A
    JOURNAL OF MATERIALS SCIENCE, 2000, 35 (24) : 6169 - 6174
  • [25] Phase equilibria in the Ti-rich corner of the Ti-Si-Sn-Al system Part I Section 9Si-1Sn (at.%)
    M. Bulanova
    A. Soroka
    P. Zheltov
    L. Tretyachenko
    K. Meleshevich
    A. Samelyuk
    Journal of Materials Science, 2000, 35 : 6169 - 6174
  • [26] Phase Equilibria in the Ternary Al-Ti-Pt System. II. Liquidus Surface of the Al-Ti-Pt System in the Compositions Range 0-50 at.% Pt
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Pavlyuchkov, D. V.
    Meleshevich, K. A.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 57 (11-12) : 709 - 715
  • [27] PHASE EQUILIBRIA IN THE TERNARY Al-Ti-PT SYSTEM. III. THE Al-Ti-PT MELTING DIAGRAM IN THE COMPOSITION RANGE 0-50 at.% PT
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 58 (1-2) : 81 - 88
  • [28] PHASE EQUILIBRIA IN THE TERNARY Al-Ti-Pt SYSTEM. IV. VERTICAL SECTIONS IN THE TERNARY Al-Ti-Pt SYSTEM IN THE COMPOSITION RANGE 0-50 at.% Pt
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 58 (5-6) : 323 - 328
  • [29] Phase stabilities and equilibria of the Ti-Al-Nb ternary system at intermediate temperatures II. The 980 °C isothermal section and reactions
    Xu, Shuai
    Lin, Junpin
    Liang, Yongfeng
    He, Jianping
    Qiao, Yi
    Cha, Limei
    Yang, Liang
    Jiang, Xianquan
    JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 940
  • [30] The Co-Ni-Zr Phase Diagram in the Zr-ZrCo-ZrNi Region I. Phase Equilibria in the Zr-ZrCo-ZrNi System at Subsolidus Temperature, 900°C, and 800°C
    Semenova, O. L.
    Petyukh, V. M.
    Fomichov, O. S.
    POWDER METALLURGY AND METAL CERAMICS, 2021, 59 (9-10) : 564 - 575
12345