Gelcasting preparation of porous silicon nitride ceramics by adjusting the content of monomers

被引：0
作者：
Juanli Yu
Hongjie Wang
Jian Zhang
Dahai Zhang
Youlan Yan
机构：
[1] Xi’an Jiaotong University,State Key Laboratory for Mechanical Behavior of Materials, School of Materials Science and Engineering
[2] National Key Laboratory of Advanced Functional Composite Materials,undefined
来源：
Journal of Sol-Gel Science and Technology | 2010年 / 53卷
关键词：
Gelcasting; Ratio of monomers; Porous Si; N; ceramics; Porosity; Strength;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The gelcasting preparation of high-performance porous Si3N4 ceramics by merely increasing monomer content in the slurry without other organic additives was presented, and the influences of monomer content and the ratio of monomers on gelcasting preparation of porous Si3N4 ceramics were investigated. The results suggest that monomer content and the ratio of monomers have great influences on the performances of green body and sintered body of porous Si3N4 ceramics, and the warpage and shrinkage of green body can be effectively improved by selecting reasonable the ratio of monomers. High-performance sintered body was achieved by high-performance green body. The pore size of porous Si3N4 ceramics is less than 1 μm, and the flexural strength and porosity are above 130 MPa and above 50%, respectively.
引用
收藏
页码：515 / 523
页数：8
相关论文
共 120 条
  • [1] Riley FL(2000)undefined J Am Ceram Soc 83 245-265
  • [2] Yang JF(2002)undefined J Am Ceram Soc 85 1512-1516
  • [3] Díaz SA(2008)undefined Mater Sci Eng A 498 5-11
  • [4] Ohji T(2005)undefined J Mater Sci Technol 21 894-898
  • [5] Zhang W(2005)undefined Acta Mater 53 2981-2990
  • [6] Wang HJ(2002)undefined J Eur Ceram Soc 22 2489-2494
  • [7] Jin ZH(2003)undefined Ceram Int 29 363-364
  • [8] Yang JF(2005)undefined J Am Ceram Soc 88 1030-1032
  • [9] Janssen R(1997)undefined J Am Ceram Soc 80 495-498
  • [10] Schneider G(2000)undefined J Am Ceram Soc 83 2094-2096
12345678910