The need to generate entropy characteristics for fatigue life prediction in low-carbon steel

被引：0
作者：
R. Idris
S. Abdullah
P. Thamburaja
M. Z. Omar
机构：
[1] Universiti Kebangsaan Malaysia (UKM),Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment
来源：
Journal of the Brazilian Society of Mechanical Sciences and Engineering | 2018年 / 40卷
关键词：
Entropy generation; Fatigue crack growth; Fatigue life prediction; Temperature evolution;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This paper presents the need to generate entropy characteristics for fatigue life prediction in low-carbon steel. Entropy generation is a manner in which the measurement of degradation can be ascertained by keeping tab of fatigue process. It helps to predict the lifespan of the specimen which undergoes repetitive cyclic load. To ensure validity, temperature evolution is measured through a fatigue crack growth test induced upon a low-carbon steel material. A thermocouple is used to keep track of the surface temperature created upon the specimen while undergoing cycles of load till it fails, thus arriving at a conclusion that the surface temperature of a specimen under fatigue crack growth test can be used to predict the fatigue point as well as the lifespan of a material. Therefore, the results show that the total entropy generation can be used to predict the fatigue life of the material. The predicted fatigue life based on temperature evolution during the fatigue crack growth test was found to be agreeable with results of the experiments.
引用
收藏
相关论文
共 82 条
  • [1] Naderi M.(2009)On the thermodynamic entropy of fatigue fracture Proceedings of the Royal Society A: Mathematical, Physical and Engineering Sciences 466 423-438
  • [2] Amiri M.(2016)Estimation study of structure crack propagation under random load based on multiple factors correction J Braz Soc Mech Sci Eng 39 681-693
  • [3] Khonsari M. M.(2010)Life prediction of metals undergoing fatigue load based on temperature evolution Mater Sci Eng A 527 1555-1559
  • [4] Lin Z(2013)Rapid determination of fatigue life based on temperature evolution Int J Fatigue 54 1-6
  • [5] Min-ping J(2012)The use of the specific heat loss to analyse the low and high-cycle fatigue behaviour of plain and notched specimens made of a stainless steel Eng Fract Mech 81 2-16
  • [6] Amiri M(2015)Analysis of temperature and fracture surface of AISI4140 steel in very high cycle fatigue regime Theor Appl Fract Mech 80 22-30
  • [7] Khonsari M(2014)Numerical evaluation of Paris-regime crack growth rate based on plastically dissipated energy Eng Fract Mech 124–125 155-166
  • [8] Zhang L(2014)FEM evaluation of the dissipated energy in front of a crack tip under 2D mixed mode loading condition Proc Mater Sci 3 673-678
  • [9] Liu XS(2014)About the effect of plastic dissipation in heat at the crack tip on the stress intensity factor under cyclic loading Int J Fatigue 58 56-65
  • [10] Wu SH(2014)Investigation of energy dissipation and plastic zone size during fatigue crack propagation in a high-alloyed steel Proc Mater Sci 3 408-413
123456789