Effect of Friction Stir Welding on the Strength of Butt Joints of Aluminum Alloy 1565ch

被引：0
作者：
Ovchinnikov V.V. [1 ]
Parfenovskaya O.A. [1 ]
Gubin A.M. [1 ]
机构：
[1] Moscow Polytechnic University, Moscow
来源：
Steel in Translation | 2023年 / 53卷 / 11期
关键词：
aluminum alloy 1565ch; defect; discontinuity; feed per revolution; friction stir welding; mode parameters; strength; structure;
D O I：
10.3103/S0967091223110244
中图分类号：
学科分类号：
摘要：
Abstract: In friction stir welding, the rotation of the tool at the joint between the metal plates causes frictional heating and metal plasticising. Processes of intense plastic deformation effect the formation of the weld microstructure, determining strength properties. However, the main factor is the specific temperature and time conditions under which the friction stir welding process is implemented. It has been established experimentally that when temperature-time parameters are violated, defects in the form of weld discontinuities are localized at the weld-base metal boundary, the formation of which is caused by the incompatibility of the weld metal deformation and the adjacent base material. It is shown that the mechanism of destruction of a welded joint is determined by the presence of defects reducing the effective cross-section of the welded joint. © Allerton Press, Inc. 2023.
引用
收藏
页码：962 / 969
页数：7
相关论文
共 50 条
[31]   The Microstructure of Aluminum A5083 Butt Joint by Friction Stir Welding [J].
Jasri, M. A. H. M. ;
Afendi, M. ;
Ismail, A. ;
Ishak, M. .
INTERNATIONAL CONFERENCE ON MATHEMATICS, ENGINEERING AND INDUSTRIAL APPLICATIONS 2014 (ICOMEIA 2014), 2015, 1660
[32]   Effect of rotational speed and double-sided welding in friction stir-welded dissimilar joints of aluminum alloy and steel [J].
Bergmann, Luciano A. ;
Batistao, Bruna Fernanda ;
de Alcantara, Nelson Guedes ;
Gargarella, Piter ;
Klusemann, Benjamin .
WELDING IN THE WORLD, 2022, 66 (09) :1747-1756
[33]   Effect of Ultrasonic Impact on the Macrostructure and Strength of Dissimilar Aluminum and Titanium Alloys Joints Produced by Friction Stir Welding [J].
Eliseev, A. A. ;
Ermakova, S. A. ;
Kolubaev, E. A. .
RUSSIAN PHYSICS JOURNAL, 2023, 65 (12) :2210-2215
[34]   Comparative numerical analysis between butt and lap joints of Mg alloy friction stir welding with considering tilted tool effect [J].
Zhai, Ming ;
Shi, Lei ;
Song, HongTu ;
Yin, JiaLin ;
Wu, ChuanSong ;
Zhao, WenZhen .
JOURNAL OF MANUFACTURING PROCESSES, 2024, 120 :951-965
[35]   Structure Modification of a Rheocast Aluminum-Zinc Alloy by Friction Stir Butt Welding: Microstructural Evolution [J].
Karimnejad, Alireza ;
Ashjari, Mehrdad ;
Heidarzadeh, Akbar ;
Saeid, Tohid .
METALS AND MATERIALS INTERNATIONAL, 2021, 27 (09) :3508-3521
[36]   Effect of Ultrasonic Impact on the Macrostructure and Strength of Dissimilar Aluminum and Titanium Alloys Joints Produced by Friction Stir Welding [J].
A. A. Eliseev ;
S. A. Ermakova ;
E. A. Kolubaev .
Russian Physics Journal, 2023, 65 :2210-2215
[37]   Effect of welding parameters on microstructure and mechanical properties of friction stir welded joints of 2060 aluminum lithium alloy [J].
Yuqing Mao ;
Liming Ke ;
Fencheng Liu ;
Chunping Huang ;
Yuhua Chen ;
Qiang Liu .
The International Journal of Advanced Manufacturing Technology, 2015, 81 :1419-1431
[38]   Effect of welding parameters on microstructure and mechanical properties of friction stir welded joints of 2060 aluminum lithium alloy [J].
Mao, Yuqing ;
Ke, Liming ;
Liu, Fencheng ;
Huang, Chunping ;
Chen, Yuhua ;
Liu, Qiang .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2015, 81 (5-8) :1419-1431
[39]   Effect of ultrasonic impact treatment on microstructure and corrosion behavior of friction stir welding joints of 2219 aluminum alloy [J].
Qian, Shuaihao ;
Zhang, Timing ;
Chen, Yuhua ;
Xie, Jilin ;
Chen, Yi ;
Lin, Tiesong ;
Li, Hongxiang .
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2022, 18 :1631-1642
[40]   Friction stir welding of high strength aluminum alloys [J].
Jata, KV .
ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 2000, 331-3 :1701-1712
12345