Surface Morphology and Properties of Diamond Etched by MnO2 Powder

被引:0
作者
Changjiang Xiao
机构
[1] Henan University of Technology,School of Material Science and Engineering
来源
Journal of Materials Engineering and Performance | 2024年 / 33卷
关键词
anisotropic etching; anchoring bonding; diamond; etching mechanism; MnO; powder; properties; surface morphology;
D O I
暂无
中图分类号
学科分类号
摘要
Synthetic diamond crystallites were successfully etched by MnO2 powder. The effect of etching behavior on the surface morphology and properties of the treated diamond crystallites was investigated. Results showed that the etching intensity of both {100} and {111} planes increased as temperature increases, and the {111} plane was etched more significantly than the {100} plane under the same conditions. After etching, the morphology of etched pits on the {100} plane transformed from quadrilateral to octagonal, while those on the {111} plane were distinguished by triangular conical bulges. The compressive strength of a single diamond particle declines from 255 to 202 N, and the impact toughness decreases from 90.11% to 86.3%. More significantly, compared with raw diamond, the maximum flexural strength of the Cu-matrix bonding diamond block with etched diamonds increased from 394.2 to 464.9 MPa, an increase of 17.9%, and the cutting ratio of the diamond saw blades decreases from 17.5 to 9.67 g/m2. The ability to produce an anchoring connection between the etched diamond and the matrix accounts for the performance increase in diamond tools. The etching mechanism is a reaction between MnO2 and the C atom on the diamond surface.
引用
收藏
页码:2231 / 2241
页数:10
相关论文
共 63 条
  • [1] Kuroshima H(2017)Mechanism of Anisotropic Etching on Diamond (111) Surfaces by a Hydrogen Plasma Treatment Appl. Surf. Sci. 422 452-455
  • [2] Makino T(2016)Preparation of Ti-Coated Diamond Particles by Microwave Heating Appl. Surf. Sci. 390 909-916
  • [3] Yamasaki S(2014)Preparation and Wear Resistance of Electrodeposited Ni-W/Diamond Composite Coatings Appl. Surf. Sci. 308 372-379
  • [4] Gu QC(2017)Effect of Electrodeposition Conditions on Structure and Mechanical Properties of Ni-W/Diamond Composite Coatings Surf. Coat. Technol. 309 337-343
  • [5] Peng JH(2018)Properties of Nano-Sic/Ni Composite Coating on Diamond Surfaces Surf. Eng. 34 832-837
  • [6] Xu L(1995)F Diam. Relat. Mater. 4 1317-1324
  • [7] Houa KH(1979), H Carbon 17 485-489
  • [8] Wang HT(2000)O, and O Philos. Mag. A 80 725-745
  • [9] Sheu HH(2010) Etching Rates of Diamond and the Effects of F Appl. Phys. Lett. 97 073117-456
  • [10] Kumar MD(2013), HF and H Carbon 59 448-212