Choosing the optimum heat treatment for cold-rolled dual-phase steel by the method of orthogonal design

被引：0
作者：
Qifeng Dai
Renbo Song
Zhifei Guo
机构：
[1] University of Science and Technology (School of Materials Science and Engineering),
[2] Shougang Research Institute of Technology,undefined
来源：
Metal Science and Heat Treatment | 2013年 / 55卷
关键词：
dual-phase steel; annealing; method of orthogonal design; cold rolling; transmission electron microscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The optimum parameters for the continuous annealing of cold-rolled dual-phase steel are determined by the method of orthogonal design to obtain an ultimate rupture strength exceeding 1000 MPa and an elongation exceeding 12%. The microstructure of the steel is studied with the help of optical and transmission electron microscopy.
引用
收藏
页码：270 / 274
页数：4
相关论文
共 39 条
[1]  
Modi AP(2007)Effects of microstructure and experimental parameters on high stress abrasive wear behaviour of a 0.19 wt.% C dual phase steel Tribol. Int. 40 490-497
[2]  
Meng Q(2009)Effect of water quenching process on microstructure and tensile properties of low alloy cold rolled dual-phase steel Mater. Design. 30 2379-2385
[3]  
Li J(2010)Heat treatment of cold-rolled low-carbon Si – Mn dual phase steels J. Iron Steel Res. Int. 17 54-58
[4]  
Wang J(2008)Effect of water quench process on mechanical properties of cold rolled dual phase steel microalloyed with niobium Mater. Lett. 62 327-329
[5]  
Luo J(2009)Development of a dual phase steel using orthogonal design method Mater. Design. 30 1251-1257
[6]  
Shi W(2002)Properties of the themomechanically processed dual-phase steels containing fibrous martensite Mater. Sci. Eng. A 35 298-308
[7]  
Huang QH(2004)On-line conversion and determination of artemisinin and its kinetic parameters using orthogonal design by coupling of flow injection with capillary electrophoresis Anal. Chim. Acta 525 239-245
[8]  
Li L(2009)Effect of continuous annealing parameters on the mechanical properties and microstructures of a cold rolled dual phase steel Int. J. Min. Met. Mater. 16 159-164
[9]  
Liang X(2010)Microstructure, texture, grain boundary characteristics and mechanical properties of a cold rolled and annealed ferrite-bainite dual phase steel Int. J. Mater. Res. 101 1252-1263
[10]  
Li J(1980)An evaluation of the importance of epitaxial ferrite in dual-phase steel microstructures Scr. Metall. 14 1239-1243
1234