Enhancement of fire performance for rigid polyurethane foam composites by incorporation of aluminum hypophosphite and expanded graphite

被引：0
作者：
Mengru Liu
Zhaohe Feng
Ruiqing Zhao
Bibo Wang
Dan Deng
Zijian Zhou
Yadong Yang
Xinliang Liu
Xiuyu Liu
Gang Tang
机构：
[1] Anhui University of Technology,School of Architecture and Civil Engineering
[2] Hangzhou Steam Turbine Company Limited,College of Resources and Environment
[3] Fujian Agriculture and Forestry University,State Key Laboratory of Fire Science
[4] University of Science and Technology of China,Department of Polymer Science and Engineering
[5] Jiaxing University,undefined
来源：
Polymer Bulletin | 2022年 / 79卷
关键词：
Rigid polyurethane foam; Composites; Expanded graphite; Aluminum hypophosphite; Flame retardant;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A series of rigid polyurethane foam/aluminum hypophosphite/expanded graphite (RPUF/AHP/EG) composites were prepared by one-step water-blown method. The effects of AHP/EG on the cell structure, thermal stability, flame retardant as well as combustion behavior of the composites were investigated by Scanning electron microscope (SEM), Thermogravimetric analysis (TG), Limiting oxygen index (LOI), UL-94 vertical burning test and Micro-combustion calorimetry (MCC). Flame-retardant tests and thermogravimetric analysis confirmed that the AHP/EG system enhanced high-temperature stability and flame-retardant performance of the composites. The char residue of RPUF/AHP15/EG15 at 700 °C was 22.4 wt%, the LOI value was 26.4 vol% with V-1 rating in UL-94 test. Thermogravimetric analysis-Fourier transform infrared spectrometer (TG-FTIR) indicated that AHP/EG system significantly inhibited the generation of hydrocarbons, CO2, CO and esters from the pyrolysis RPUF matrix. XPS analysis showed that the combination of AHP and EG could promote RPUF matrix to form aromatic and aromatic heterocyclic structure, which was benefit to the formation of dense char layer, thus achieving the purpose of flame retardancy. Based on the analysis, the flame-retardant mechanism of RPUF/AHP/EG composites was proposed.
引用
收藏
页码：10991 / 11012
页数：21
相关论文
共 235 条
[1]  
Visakh PM(2019)Review on soft polyurethane flame retardant Constr Build Mater 227 116673-121166
[2]  
Semkin AO(2021)Phosphorus-containing soybean oil-derived polyols for flame-retardant and smoke-suppressant rigid polyurethane foams Polym Degrad Stabil. 191 109701-355
[3]  
Rezaev IA(2020)Preparation of Zeolitic Imidazolate Frameworks and Their Application as Flame Retardant and Smoke Suppression Agent for Rigid Polyurethane Foam Polymers 12 347-287
[4]  
Fateev AV(2020)Steel slag waste combined with melamine pyrophosphate as a flame retardant for rigid polyurethane foams Adv Powder Technol 31 279-7
[5]  
Tang G(2018)Flame-retardant and mechanical properties of rigid polyurethane foam/MRP/mg(OH)2/GF/HGB composites J Appl Polym Sci 135 46551-1280
[6]  
Liu MR(2014)Environmentally Friendly Flame-Retardant and Its Application in Rigid Polyurethane Foam Int J Polym Sci 2014 1-109
[7]  
Deng D(2021)A phosphorus-based bi-functional flame retardant for rigid polyurethane foam Polym Degrad Stabil 186 109516-545
[8]  
Zhao RQ(2021)Self-extinguishing and transparent epoxy resin modified by a phosphine-containing bio-based derivative Front Chem Sci Eng 15 1269-9
[9]  
Liu XL(2015)Synthesis, mechanical properties and fire behaviors of rigid polyurethane foam with a reactive flame retardant containing phosphazene and phosphate Polym Degrad Stabil 122 102-43
[10]  
Yang YD(2020)Interface Engineering of MXene towards Super-tough and Strong Polymer Nanocomposites with High Ductility and Excellent Fire Safety Chem Eng J 399 125829-E1014
12345678910