Effect of Silica Ratio on the Corrosion Behavior of Nano-silica Potassium Silicate Coatings on Aluminum Alloy 2024

被引：0
作者：
H. Bahri
I. Danaee
G. R. Rashed
D. Zaarei
机构：
[1] Petroleum University of Technology,Abadan Faculty of Petroleum Engineering
[2] Islamic Azad University,Technical Faculty, South Tehran Branch
来源：
Journal of Materials Engineering and Performance | 2015年 / 24卷
关键词：
aluminum 2024; corrosion; nano-silica; silicate conversion coatings;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Nano-silica modified potassium silicate conversion coating was deposited in different nano-silica/potassium silicate ratios on the surface of 2024 aluminum alloy. The corrosion behavior of coatings was studied by electrochemical impedance spectroscopy, current transient, potentiodynamic polarization, and surface techniques. The ratio of nano-silica/potassium silicate was optimized in order to obtain higher corrosion protection. The experimental results indicated that with increasing nano-silica/potassium silicate ratio, the corrosion resistance of aluminum increases. Furthermore, the pitting corrosion probability of potassium silicate conversion coating decreased with increasing silica ratio. This can be related to the size of nano-silica particles and the ability to fill the pores in potassium silicate coating and reinforce the created siloxane bridges.
引用
收藏
页码：839 / 847
页数：8
相关论文
共 150 条
[1]  
Wang Z(2013)Determination and Relaxation of Residual Stress in 2024 Al-30 vol.% Magnesium Borate Whisker Composites J. Mater. Eng. Perform. 22 3126-3133
[2]  
Jiang Z(2009)The Effect of Inhibitors on the Susceptibility of Al 6013/SiC Interface to Localized Corrosion J. Mater. Eng. Perform. 18 129-136
[3]  
Hu H(2013)Reciprocating Wear Resistance of Al-SiC Nano-composite Fabricated by Accumulative Roll Bonding Process Mater. Des. 50 497-502
[4]  
Nie X(2013)Optimization of FS Welding Parameters for Improving Mechanical Behavior of AA2024-T351 Joints Based on Taguchi Method J. Mater. Eng. Perform. 22 2261-2270
[5]  
Ahmad Z(2011)Mechanical Properties and Welding Power of Friction Stirred AA2024-T35 Joints J. Mater. Eng. Perform. 20 839-845
[6]  
Abdul Aleem BJ(2009)Coating Cure Temperatures on the Mechanical Properties of Aluminum Alloy Substrates J. Mater. Eng. Perform. 18 70-78
[7]  
Darmiani E(2011)Degradation Modeling of 2024 Aluminum Alloy During Corrosion Process J. Mater. Eng. Perform. 20 348-354
[8]  
Danaee I(2011)Inhibition of Tryptophan on AA 2024 in Chloride-Containing Solutions J. Mater. Eng. Perform. 20 265-270
[9]  
Golozar MA(2007)The Effect of Surface Engineering Treatments on the Fatigue Behavior of 2024-T351 Aluminum Alloy J. Mater. Eng. Perform. 16 30-34
[10]  
Toroghinejad MR(2013)Influence of Combined Loading on Microstructure and Properties of Aluminum Alloy 2024-T3 J. Mater. Eng. Perform. 22 3421-3429
12345678910