Influence of the Matrix Type on the Mode I Fracture of Carbon-Epoxy Composites Under Dynamic Delamination

被引：0
|
作者：
A. Argüelles
J. Viña
A. F. Canteli
A. Lopez
机构：
[1] University of Oviedo,Department of Construction and Manufacturing Engineering
[2] University de Oviedo,Department of Materials Science and Metallurgical Engineering
来源：
Experimental Mechanics | 2011年 / 51卷
关键词：
Delamination; Mode I; Fracture; Fatigue; Matrix;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The delamination energy and fracture behaviour under static and dynamic mode I loading of two composites, made of the same unidirectional carbon reinforcement embedded in two different matrices, one tough and the other brittle, was investigated with the aim of analyzing the influence of the employed resin on the fatigue delamination behaviour of both composites. In the case of dynamic loading, the number of cycles necessary for the onset of delamination was determined for a given elastic energy release rate and crack growth rate for different critical energy rates. The double cantilever beam (DCB) test was found to be suitable for promoting the initial delamination. The experimental results confirm the enhanced performance of the tough resin both in terms of crack initiation and growth rate.
引用
收藏
页码：293 / 301
页数：8
相关论文
共 50 条
  • [41] Moisture effects on Mode II delamination behavior of carbon/epoxy composites
    Zhao, SX
    Gaedke, M
    ADVANCED COMPOSITE MATERIALS, 1996, 5 (04) : 291 - 307
  • [42] Dynamic mode II interlaminar fracture toughness of electrically modified carbon/epoxy composites
    Shamchi, Sahand P.
    de Moura, Marcelo F. S. F.
    Zhao, Zhongjie
    Yi, Xiaosu
    Moreira, Pedro M. G. P.
    INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2022, 159
  • [43] Effects of fiber orientation of adjacent plies on the mode I crack propagation in a carbon-epoxy laminates
    Rehan, M. S. Mohamed
    Rousseau, J.
    Gong, X. J.
    Guillaumat, L.
    Ali, J. S. M.
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10 : 3179 - 3184
  • [44] Fractography and failure mechanisms in static mode I and mode II delamination testing of unidirectional carbon reinforced composites
    Bonhomme, J.
    Arguelles, A.
    Vina, J.
    Vina, I.
    POLYMER TESTING, 2009, 28 (06) : 612 - 617
  • [45] Mode-I interlaminar fracture of carbon/epoxy cross-ply composites
    de Morais, AB
    de Moura, MF
    Marques, AT
    de Castro, PT
    COMPOSITES SCIENCE AND TECHNOLOGY, 2002, 62 (05) : 679 - 686
  • [46] INFLUENCE OF PLY ORIENTATION ON INTERLAMINAR FRACTURE TOUGHNESS OF CARBON/EPOXY COMPOSITES
    Prodduturi, Ashok Kumar
    Pinninti, Ravinder Reddy
    Avss, Kumara Swami Gupta
    COMPOSITES-MECHANICS COMPUTATIONS APPLICATIONS, 2024, 15 (03): : 25 - 34
  • [47] Mode I delamination behaviour of short fibre reinforced carbon fibre/epoxy composites following environmental conditioning
    Walker, L
    Hu, XZ
    COMPOSITES SCIENCE AND TECHNOLOGY, 2003, 63 (3-4) : 531 - 537
  • [48] Study of Fatigue Behavior of Epoxy-Carbon Composites under Mixed Mode I/II Loading
    Rocandio, Clara
    Vina, Jaime
    Arguelles, Antonio
    Rubiera, Silvia
    ADVANCED ENGINEERING MATERIALS, 2018, 20 (02)
  • [49] Influence of the Mode Mixity Ratio and Test Procedures on the Total Energy Release Rate in Carbon-Epoxy Laminates
    Mollon, V.
    Vina, J.
    Argueelles, A.
    Bonhomme, J.
    Vina, I.
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
  • [50] Mode-I interlaminar fracture toughness in unidirectional carbon-fibre/epoxy composites
    Barikani, M
    Saidpour, H
    Sezen, M
    IRANIAN POLYMER JOURNAL, 2002, 11 (06) : 413 - 423
12345