Influence of the Matrix Type on the Mode I Fracture of Carbon-Epoxy Composites Under Dynamic Delamination

被引：0
|
作者：
A. Argüelles
J. Viña
A. F. Canteli
A. Lopez
机构：
[1] University of Oviedo,Department of Construction and Manufacturing Engineering
[2] University de Oviedo,Department of Materials Science and Metallurgical Engineering
来源：
Experimental Mechanics | 2011年 / 51卷
关键词：
Delamination; Mode I; Fracture; Fatigue; Matrix;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The delamination energy and fracture behaviour under static and dynamic mode I loading of two composites, made of the same unidirectional carbon reinforcement embedded in two different matrices, one tough and the other brittle, was investigated with the aim of analyzing the influence of the employed resin on the fatigue delamination behaviour of both composites. In the case of dynamic loading, the number of cycles necessary for the onset of delamination was determined for a given elastic energy release rate and crack growth rate for different critical energy rates. The double cantilever beam (DCB) test was found to be suitable for promoting the initial delamination. The experimental results confirm the enhanced performance of the tough resin both in terms of crack initiation and growth rate.
引用
收藏
页码：293 / 301
页数：8
相关论文
共 50 条
  • [31] Mode II fracture characterization of a hybrid cork/carbon-epoxy laminate
    de Moura, M. F. S. F.
    Fernandes, R.
    Silva, F. G. A.
    Dourado, N.
    COMPOSITES PART B-ENGINEERING, 2015, 76 : 44 - 51
  • [32] MIXED-MODE DELAMINATION BEHAVIOR OF CARBON/EPOXY COMPOSITES
    ZHAO, S
    GADKE, M
    PRINZ, R
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1995, 14 (08) : 804 - 826
  • [33] Influence of loading rate on the delamination response of untufted and tufted carbon epoxy non crimp fabric composites: Mode I
    de Verdiere, M. Colin
    Skordos, A. A.
    May, M.
    Walton, A. C.
    ENGINEERING FRACTURE MECHANICS, 2012, 96 : 11 - 25
  • [34] The Influence of Carbon/Glass/Epoxy Hybrid Interfacial Adhesion on the Mode II Delamination Fracture Toughness
    F. M. Monticeli
    H. L. Ornaghi
    M. O. H. Cioffi
    H. J. C. Voorwald
    Mechanics of Composite Materials, 2022, 58 : 237 - 248
  • [35] Repairing wood beams under bending using carbon-epoxy composites
    Dourado, N.
    Pereira, F. A. M.
    de Moura, M. F. S. F.
    Morais, J. J. L.
    ENGINEERING STRUCTURES, 2012, 34 : 342 - 350
  • [36] Influence of the principal tensile stresses on delamination fracture mechanisms and their associated morphology for different loading modes in carbon/epoxy composites
    Mollon, V.
    Bonhomme, J.
    Vina, J.
    Argueelles, A.
    Fernandez-Canteli, A.
    COMPOSITES PART B-ENGINEERING, 2012, 43 (03) : 1676 - 1680
  • [37] Effect of particle size on mixed-mode fracture of nanographene reinforced epoxy and mode I delamination of its carbon fiber composite
    Roy, Samit
    Kumar, Abhishek
    COMPOSITE STRUCTURES, 2017, 181 : 1 - 8
  • [38] Dynamic fracture of carbon nanotube/epoxy composites under high strain-rate loading
    Bie, B. X.
    Han, J. H.
    Lu, L.
    Zhou, X. M.
    Qi, M. L.
    Zhang, Z.
    Luo, S. N.
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2015, 68 : 282 - 288
  • [39] Moisture Absorption Effects on Mode II Delamination of Carbon/Epoxy Composites
    Wong, King Jye
    Johar, Mahzan
    Koloor, Seyed Saeid Rahimian
    Petru, Michal
    Tamin, Mohd Nasir
    POLYMERS, 2020, 12 (09)
  • [40] Influence of sprayed multi-walled carbon nanotubes on mode I and mode II interlaminar fracture toughness of carbon fiber/epoxy composites
    Rodriguez-Gonzalez, J. A.
    Rubio-Gonzalez, C.
    ADVANCED COMPOSITE MATERIALS, 2019, 28 (sup1) : 19 - 36
12345