Preparation and properties of FeZrB amorphous-nanocrystalline soft magnetic alloy

被引：0
作者：
Zhong Hua
Yaming Sun
Maobin Wei
Wanqiu Yu
机构：
[1] Jilin Normal University,College of Physics
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2009年 / 24卷
关键词：
FeZrB amorphous-nanocrystalline alloy; grain size; specific saturation magnetization;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Fe68Zr20B12 amorphous alloy was prepared by mechanical alloying(MA) method and annealed at different temperatures. Microstructures and magnetic properties of Fe68Zr20B12 alloys as-milled and annealed at 693, 843, 943 and 993 K were studied. The raw powders(Fe, Zr, B) formed b. c. c. α-Fe solid solution at early stages of MA and then transformed into amorphous alloy. Grain size(D) of Fe68Zr20B12 alloys increases with increasing annealing temperature and keeps at nanometer level. The specific saturation magnetization(σs) increases with increasing annealing temperature from 300 K to 943 K, and then decreases with annealing temperature at 993 K because of the precipitation of Fe3B.
引用
收藏
页码：747 / 749
页数：2
相关论文
共 27 条
  • [1] Makino A.(1997)Nanocrystalline Soft Magnetic Fe-M-B(M=Zr, Hf, Nb) Alloys and their Applications[J] Mater. Sci. Eng. A226–228 594-602
  • [2] Hatanai T.(1994)Magnetic Properties and Microstructure of Nanocrystalline bcc Fe-M-B(M=Zr, Hf, Nb) Alloys[J] J. Magn. Magn. Mater 133 329-333
  • [3] Inoue A.(1991)Effect of Composition on Curie Temperature, Magnetic Moment, and High-field Susceptibility of Amorphous Fe Phys. Rev. B 43 11005-11009
  • [4] Makino A.(2003)M J. Magn. Magn. Mater. 254 466-468
  • [5] Suzuki K.(2002)Zr J. Alloys. Compounds 339 221-229
  • [6] Inoue A.(2001) (M=V, Cr, Mn, Co, Ni, Cu, Si, and B) Alloys[J] Scripta Mater. 44 2729-2734
  • [7] Shen B. G.(2002)Magnetoimpedance Effect in Nanocrystalline FeZrNbB Ribbons[J] Metallic Functional Materials 9 34-37
  • [8] Xu R. F.(2006)Phase Transformations in the Fe(Co, Ni)ZrB Alloys Induced by Ball Milling[J] Materials Letters 60 1080-1084
  • [9] Zhao G. J.(2004)Influences of Oxide Phases on the Coercivity of Mechanically Alloyed Multicomponent Fe-based Amorphous Alloys[J] Journal of Northeastern University 25 1072-1075
  • [10] Gona M. N.(undefined)Magnetic Properties of (Fe undefined undefined undefined-undefined
123