Improvement of creep strength of advanced ferritic steel welded joints

被引:0
作者
Abe F. [1 ]
Tabuchi M. [1 ]
Kondo M. [1 ]
Tsukamoto S. [1 ]
机构
[1] National Institute for Materials Science (NIMS),
关键词
Arc welding; Creep resisting materials; Creep strength; Creep tests; EB welding; Gas shielded arc welding; GTA welding; Heat affected zone; Mechanical properties; Mechanical tests; Microstructure; Parent material; Steels; Strength; Weld zone; Welded joints;
D O I
10.1007/BF03263424
中图分类号
学科分类号
摘要
The microstructure and creep strength of simulated HAZ specimens and welded joints have been investigated for advanced 9-12 %Cr steels in order to make clear the mechanisms responsible for Type IV crack and to improve the creep strength of welded joints at high temperature. Creep and creep rupture tests were carried out at 650°C (923 K) for up to about 104 h. Creep crack growth tests were also carried out using CT specimens. The creep rupture time of simulated HAZ specimens has its minimum after heating to AC3 temperature, which produces fine-grained microstructure. Reducing the width of HAZ by means of EB welding is effective for the extension of creep life but the brittle Type IV fracture appears even in the EB welded joints at low stress and long time conditions. The welded joint specimens were fractured in fine-grained HAZ and resulted in shorter creep life than those of base metal due to the formation of creep voids and cracks. Using a specially-designed FEM code for Type IV crack growth behaviour, the effect of creep ductility and void formation ahead of the crack tip on creep crack growth rate is successfully simulated. The Type IV fracture is suppressed by the addition of boron, which suppresses the formation of fine-grained region in HAZ.
引用
收藏
页码:59 / 66
页数:7
相关论文
共 50 条
[41]   Fatigue Strength Assessment of Welded Mild Steel Joints Containing Bulk Imperfections [J].
Leitner, Martin ;
Murakami, Yukitaka ;
Farajian, Majid ;
Remes, Heikki ;
Stoschka, Michael .
METALS, 2018, 8 (05)
[42]   Microstructure and properties of fiber laser welded high strength steel butt joints [J].
Zong Xuewen ;
Wang Kaiming ;
Fu Hanguang .
MATERIALS TESTING, 2020, 62 (02) :172-176
[43]   Experimental study on the behavior of mismatched butt welded joints of high strength steel [J].
Ran, Ming-Ming ;
Sun, Fei-Fei ;
Li, Guo-Qiang ;
Kanvinde, Amit ;
Wang, Yan-Bo ;
Xiao, Robert Y. .
JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2019, 153 :196-208
[44]   Fatigue Crack Propagation Rate of High Strength Steel's Welded Joints [J].
Li, Hong-Tao ;
Song, Xu-Ding .
PROCEEDINGS OF THE 2ND ANNUAL INTERNATIONAL CONFERENCE ON ADVANCED MATERIAL ENGINEERING (AME 2016), 2016, 85 :450-456
[45]   Degradation of creep strength in welded joint of 9%Cr steel [J].
Matsui, M ;
Tabuchi, M ;
Watanabe, T ;
Kubo, K ;
Kinugawa, J ;
Abe, F .
ISIJ INTERNATIONAL, 2001, 41 :S126-S130
[46]   Investigating the effect of ferritic filler materials on the mechanical and metallurgical properties of Hardox 400 steel welded joints [J].
Gupta, Ajay ;
Sharma, Varun ;
Kumar, Parul ;
Thakur, Ankit .
MATERIALS TODAY-PROCEEDINGS, 2021, 39 :1640-1646
[47]   Microstructure and mechanical properties of friction stir welded joints of reduced activation ferritic-martensitic steel [J].
Zhang C. ;
Cui L. ;
Liu Y. ;
Wang D. ;
Zhou M. .
Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (06) :52-57
[48]   Corrosion Behavior of Metal Active Gas Welded Joints of a High-Strength Steel for Automotive Application [J].
Garcia, Maina Portella ;
Mantovani, Gerson Luiz ;
Kumar, R. Vasant ;
Antunes, Renato Altobelli .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (10) :4718-4731
[49]   Fatigue behaviour of butt welded joints in a high strength steel [J].
Costa, J. D. M. ;
Ferreira, J. A. M. ;
Abreu, L. P. M. .
FATIGUE 2010, 2010, 2 (01) :697-705
[50]   Improvement of Microstructure Stability during Creep in High Cr Ferritic Heat Resistant Steel HAZ [J].
Tsukamoto, S. ;
Liu, Y. ;
Shirane, T. ;
Tabuchi, M. ;
Abe, F. .
TRENDS IN WELDING RESEARCH: PROCEEDINGS OF THE 9TH INTERNATIONAL CONFERENCE, 2013, :1-10