Improvement of electrochemical properties of LiNi1/3Mn1/3Co1/3O2 by coating with La0.4Ca0.6CoO3

被引：0
作者：
Jiang Du
Zhengfu Zhang
Jinhui Peng
Yamei Han
Yi Xia
Shenghui Guo
Shaohua Ju
Chongyan Leng
Guo Chen
Lei Xu
Junsai Sun
Hongge Yan
机构：
[1] Kunming University of Science and Technology,Faculty of Materials Science and Engineering
[2] National Local Joint Engineering Laboratory of Engineering Applications of Microwave Energy and Equipment Technology,Key Laboratory of Unconventional Metallurgy, Ministry of Education
[3] Kunming University of Science and Technology,College of Materials Science and Engineering
[4] Hunan University,undefined
来源：
Journal of Solid State Electrochemistry | 2014年 / 18卷
关键词：
LiNi; Co; Mn; O; Coating; Cathode; Lithium ion battery; Electrochemical properties;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this paper, La0.4Ca0.6CoO3-coated LiNi1/3Mn1/3Co1/3O2 is successfully prepared by the sol–gel method associated with microwave pyrolysis method. The structure and electrochemical properties of the La0.4Ca0.6CoO3-coated LiNi1/3Co1/3Mn1/3O2 are investigated by using X-ray diffraction (XRD), electrochemical impedance spectroscopy (EIS), and charge/discharge tests. XRD analyses show that the La0.4Ca0.6CoO3 coating does not change the structure of LiNi1/3Co1/3Mn1/3O2. The electrochemical performance studies demonstrate that 2 wt.% La0.4Ca0.6CoO3-coated LiNi1/3Co1/3Mn1/3O2 powders exhibit the best electrochemical properties, with an initial discharge capacity of 156.9 mAh g–1 and capacity retention of 98.9 % after 50 cycles when cycled at a current density of 0.2 C between 2.75 and 4.3 V. La0.4Ca0.6CoO3 coating can improve the rate performance because of the enhancement of the surface electronic/ionic transportation by the coating layer. EIS results suggest that the coating La0.4Ca0.6CoO3 plays an important role in suppressing the increase of cell impedance with cycling especially for the increase of charge-transfer resistance.
引用
收藏
页码：2211 / 2216
页数：5
相关论文
共 159 条
[11]  
Dahbi M(2008)undefined J Solid State Electrochem 12 867-872
[12]  
Wikberg JM(2009)undefined J Power Sources 188 564-569
[13]  
Saadoune I(2006)undefined Electrochim Acta 52 1316-1322
[14]  
Gustafsson TR(2009)undefined Electrochim Acta 54 5796-5803
[15]  
Svedlindh P(2008)undefined J Power Sources 178 826-831
[16]  
Edström K(2006)undefined J Power Sources 161 623-627
[17]  
Vetter J(2006)undefined Electrochim Acta 52 643-648
[18]  
Novak P(2011)undefined J Electrochem Soc 158 A883-A889
[19]  
Wagner MR(2011)undefined Nonferrous Met Soc China 21 1111-1117
[20]  
Veit C(2013)undefined Trans Nonferrous Met Soc China 23 2971-2976
12345678910