Corrosion Inhibition of l-Methionine Amino Acid as a Green Corrosion Inhibitor for Stainless Steel in the H2SO4 Solution

被引：0
作者：
M. Yeganeh
I. Khosravi-Bigdeli
M. Eskandari
S. R. Alavi Zaree
机构：
[1] Shahid Chamran University of Ahvaz,Department of Materials Science and Engineering, Faculty of Engineering
来源：
Journal of Materials Engineering and Performance | 2020年 / 29卷
关键词：
309S stainless steel; corrosion inhibitor; -Methionine (LMT);
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This study investigated the effect of l-methionine (LMT) on the corrosion behavior of AISI309S stainless steel in 1 M H2SO4 solution using electrochemical impedance spectroscopy (EIS), Tafel polarization, and electrochemical noise methods. The performance of corrosion inhibition was analyzed by scanning electron microscopy, atomic force microscopy, adsorption isotherms, x-ray photoelectron spectroscopy (XPS), and contact angle measurement. The electrochemical studies revealed a significant increase in the charge transfer resistance and a reduction in the corrosion current density in the presence of LMT in the acidic media. The results of the EIS and Tafel tests determined the corrosion inhibition efficiency to be about 97% and 95%, respectively. The microscopy analysis showed that the surface suffered lower corrosion damages in the presence of LMT. Besides, the adsorption of LMT on the anodic sites of the surface through its sulfur atom was verified by EIS and XPS studies.
引用
收藏
页码：3983 / 3994
页数：11
相关论文
共 211 条
  • [1] Mobin M(2017)Synergistic Effect of Sodium Dodecyl Sulfate and Cetyltrimethyl Ammonium Bromide on the Corrosion Inhibition Behavior of Arab. J. Chem. 10 S1364-S1372
  • [2] Parveen M(2018)-Methionine on Mild Steel in Acidic Medium Egypt. J. Pet. 27 1157-1165
  • [3] Rafiquee MZA(2017)The Use of Amino Acids as Corrosion Inhibitors for Metals: A Review Port. Electrochim. Acta 35 13-25
  • [4] Hamadi L(2002)Corrosion Inhibition of Carbon Steel in Well Water by J. Chem. Technol. Biotechnol. 77 486-494
  • [5] Mansouri S(2009)-Cysteine-Zn J. Solid State Electrochem. 13 1743-1756
  • [6] Oulmi K(2017) System J. Mol. Liq. 246 112-118
  • [7] Kareche A(2010)Effect of Amino Acids Containing Sulfur on the Corrosion of Mild Steel in Phosphoric Acid Solutions Polluted with Cl J. Mater. Sci. 45 6255-6265
  • [8] Thangakani JA(2018), F J. Mol. Liq. 272 528-538
  • [9] Rajendran S(2013) and Fe Electrochim. Acta 108 860-866
  • [10] Sathiabama J(2017) Ions—Behaviour Near and at the Corrosion Potential Arab. J. Chem. 37 1191-1200
12345678910