A transmission electron microscopy study of constituent-particle-induced corrosion in 7075-T6 and 2024-T3 aluminum alloys

被引：0
作者：
Robert P. Wei
Chi-Min Liao
Ming Gao
机构：
[1] Lehigh University,the Department of Mechanical Engineering and Mechanics
[2] China Steel Corporation,Mobil Exploration & Producing Center (MEPTEC)
[3] Material,undefined
[4] Corrosion and Inspection Group,undefined
来源：
Metallurgical and Materials Transactions A | 1998年 / 29卷
关键词：
Material Transaction; Constituent Particle; Galvanic Coupling; Thin Foil Specimen; Matrix Dissolution;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
To better understand particle-induced pitting corrosion in aluminum alloys, thin foil specimens of 7075-T6 and 2024-T3 aluminum alloys, with identified constituent particles, were immersed in aerated 0.5M NaCl solution and then examined by transmission electron microscopy (TEM). The results clearly showed matrix dissolution around the iron- and manganese-containing particles (such as Al23CuFe4), as well as the Al2Cu particles. While Al2CuMg particles tended to dissolve relative to the matrix, limited local dissolution of the matrix was also observed around these particles. These results are consistent with scanning electron microscopy (SEM) observations of pitting corrosion and are discussed in terms of the electrochemical characteristics of the particles and the matrix.
引用
收藏
页码：1153 / 1160
页数：7
相关论文
共 29 条
  • [1] Chen G.S.(1996)undefined Corrosion 52 8-15
  • [2] Gao M.(1996)undefined Mater. Sci. Eng. A219 126-32
  • [3] Wei R.P.(1994)undefined Fat. Fract. Eng. Mater. Struct. 17 1247-1247
  • [4] Chen S.(1996)undefined Scripta Mater. 35 1341-46
  • [5] Wan K.-C.(1971)undefined Corrosion 27 223-223
  • [6] Gao M.(1973)undefined Corr. Sci. 13 237-237
  • [7] Wei R.P.(1969)undefined J. Electrochem. Soc. 116 906-906
  • [8] Flournoy T.H.(1971)undefined Br. Corros. J. 6 200-200
  • [9] Piascik R.S.(1987)undefined Corrosion 43 219-219
  • [10] Willard S.A.(1998)undefined Metall. Mater. Trans. A 29A 1145-51
123