Nitride-Based ultraviolet metal-semiconductor-metal photodetectors with a low-temperature GaN layer

The GaN metal-semiconductor-metal (MSM) ultraviolet (UV) photodetectors with a low-temperature (LT)-GaN layer have been demonstrated. It was found that we could achieve a two orders of magnitude smaller, photodetector-dark current by introducing a LT-GaN layer, which could be attributed to the larger Schottky-barrier height between the Ni/Au metal contact and the LT-GaN layer. It was also found that photodetectors with the LT-GaN layer could provide a larger photocurrent to dark-current contrast ratio and a larger UV-to-visible rejection ratio. The maximum responsivity was found to be 3.3 A/W and 0.13 A/W when the photodetector with a LT-GaN layer was biased at 5 V and 1 V, respectively.