Phase equilibria in the Lu-Pd system in the composition range 0-50 at % Lu

被引：5
|
作者：
Kolchugina N.B. [1 ]
Burkhanov G.S. [1 ]
Drapala J. [2 ]
机构：
[1] Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences, Moscow 119991
[2] VysokáŠkola Báská-Technical University, Ostrava-Poruba 70833
来源：
Russian Metallurgy (Metally) | 2011年 / 2011卷 / 7期
关键词：
Differential Thermal Analysis; Composition Range; RUSSIAN Metallurgy; Differential Thermal Analysis Curve; Lutetium;
D O I：
10.1134/S0036029511070068
中图分类号：
学科分类号：
摘要：
X-ray diffraction, differential thermal analysis, and electron microscopy are used to study the crystal structures and formation sequence of intermetallics in the Lu-Pd system in a composition range of Pd-(0-50 at %) Lu. The alloys are synthesized using high-purity lutetium. Within the composition range under study, the system is characterized by terminal Pd-based solid solutions with a lutetium content up to 10 at % Lu (at 1000°C) and a number of intermetallics (Lu3Pd4, Lu2Pd3, LuPd, LuPd3, Lu10Pd21). A nonequilibrium bertholide phase is found to form in the composition range from 30 to 45 at % Lu. The phase diagram is given in the composition range Pd-(0-50 at %) Lu. © 2011 Pleiades Publishing, Ltd.
引用
收藏
页码：634 / 639
页数：5
相关论文
共 50 条
  • [11] PHASE EQUILIBRIA IN THE TERNARY Al-Ti-Pt SYSTEM. IV. VERTICAL SECTIONS IN THE TERNARY Al-Ti-Pt SYSTEM IN THE COMPOSITION RANGE 0-50 at.% Pt
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 58 (5-6) : 323 - 328
  • [12] Effect of Oxygen Pressure on Phase Equilibria in the Lu–Mn–O System
    L. B. Vedmid'
    V. F. Balakirev
    A. M. Yankin
    Yu. V. Golikov
    O. M. Fedorova
    Glass Physics and Chemistry, 2004, 30 : 345 - 348
  • [13] Phase equilibria of the GeTe-Bi2Te3 quasi-binary system in the range 0-50 mol% Bi2Te3
    Alakbarova, T. M.
    Meyer, Hans-Juergen
    Orujlu, E. N.
    Amiraslanov, I. R.
    Babanly, M. B.
    PHASE TRANSITIONS, 2021, 94 (05) : 366 - 375
  • [14] Effect of oxygen pressure on phase equilibria in the Lu-Mn-O system
    Vedmid, LB
    Balakirev, VF
    Yankin, AM
    Golikov, YV
    Fedorova, OM
    GLASS PHYSICS AND CHEMISTRY, 2004, 30 (04) : 345 - 348
  • [15] Phase Equilibria in the Lu ― V ― B System and the Structure of the New Boride Lu1.34V1.66B6
    Yurii B. Kuz'ma
    Powder Metallurgy and Metal Ceramics, 2002, 41 : 162 - 168
  • [16] Phase Equilibria in the Ternary Al-Ti-Pt System. I. Solidus Surface of the Al-Ti-Pt System in the Range 0-50 at.% Pt
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Meleshevich, K. A.
    Pavlyuchkov, D. V.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 57 (9-10) : 587 - 595
  • [17] PHASE-EQUILIBRIA IN THE HF-RH ALLOYS IN THE REGION OF 0-50 PERCENT RH ATOMIC CONTENT
    EREMENKO, VN
    SHTEPA, TD
    VELIKANOVA, TA
    DOPOVIDI AKADEMII NAUK UKRAINSKOI RSR SERIYA A-FIZIKO-MATEMATICHNI TA TECHNICHNI NAUKI, 1985, (10): : 70 - 72
  • [18] Phase Diagram of the Lu-Lu2S3 System
    Andreev, O. V.
    Parshukov, N. N.
    Kuz'micheva, G. M.
    Sekerin, S. S.
    RUSSIAN JOURNAL OF INORGANIC CHEMISTRY, 1999, 44 (06) : 962 - 965
  • [19] PHASE-DIAGRAM FOR COBALT-BERYLLIUM ALLOYS IN RANGE OF 0-50 AT-PERCENT-CO
    PUGACHEV, NS
    VERKHOROBIN, LF
    MATJUSHENKO, NN
    ALEKSENKO, IV
    DOPOVIDI AKADEMII NAUK UKRAINSKOI RSR SERIYA A-FIZIKO-MATEMATICHNI TA TECHNICHNI NAUKI, 1977, (12): : 1135 - 1137
  • [20] Phase Equilibria in the Ternary Al-Ti-Pt System. II. Liquidus Surface of the Al-Ti-Pt System in the Compositions Range 0-50 at.% Pt
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Pavlyuchkov, D. V.
    Meleshevich, K. A.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 57 (11-12) : 709 - 715
12345