Phase equilibria in the Lu-Pd system in the composition range 0-50 at % Lu

被引：5
|
作者：
Kolchugina N.B. [1 ]
Burkhanov G.S. [1 ]
Drapala J. [2 ]
机构：
[1] Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences, Moscow 119991
[2] VysokáŠkola Báská-Technical University, Ostrava-Poruba 70833
来源：
Russian Metallurgy (Metally) | 2011年 / 2011卷 / 7期
关键词：
Differential Thermal Analysis; Composition Range; RUSSIAN Metallurgy; Differential Thermal Analysis Curve; Lutetium;
D O I：
10.1134/S0036029511070068
中图分类号：
学科分类号：
摘要：
X-ray diffraction, differential thermal analysis, and electron microscopy are used to study the crystal structures and formation sequence of intermetallics in the Lu-Pd system in a composition range of Pd-(0-50 at %) Lu. The alloys are synthesized using high-purity lutetium. Within the composition range under study, the system is characterized by terminal Pd-based solid solutions with a lutetium content up to 10 at % Lu (at 1000°C) and a number of intermetallics (Lu3Pd4, Lu2Pd3, LuPd, LuPd3, Lu10Pd21). A nonequilibrium bertholide phase is found to form in the composition range from 30 to 45 at % Lu. The phase diagram is given in the composition range Pd-(0-50 at %) Lu. © 2011 Pleiades Publishing, Ltd.
引用
收藏
页码：634 / 639
页数：5
相关论文
共 50 条
  • [1] Phase diagram of Lu-Pd system in the 0-25 at. % Lu region
    Burkhanov, GS
    Ilyushin, AS
    Kol'chugina, NB
    Khatanova, NA
    Chistyakov, OD
    Tsetsgeegiin, O
    RUSSIAN METALLURGY, 1999, (06): : 132 - 136
  • [2] Lu-Pd (Lutetium-Palladium)
    Okamoto, H.
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2009, 30 (01) : 121 - 122
  • [3] Lu-Pd (Lutetium-Palladium)
    H. Okamoto
    Journal of Phase Equilibria and Diffusion, 2009, 30 : 121 - 122
  • [4] PHASE-EQUILIBRIA DIAGRAM FOR NEODYMIUM-TIN SYSTEM WITHIN A RANGE OF 0-50 AT PERCENT-SN
    EREMENKO, VN
    KHARKOVA, AM
    OBUSHENKO, IM
    DOPOVIDI AKADEMII NAUK UKRAINSKOI RSR SERIYA A-FIZIKO-MATEMATICHNI TA TECHNICHNI NAUKI, 1978, (12): : 1132 - 1136
  • [5] X-ray diffraction study of phases in the system CaS-Lu2S3 (0-50 mol % Lu2S3)
    Kuz'micheva, G. M.
    Andreev, O. V.
    RUSSIAN JOURNAL OF INORGANIC CHEMISTRY, 2008, 53 (02) : 308 - 312
  • [6] X-ray diffraction study of phases in the system CaS-Lu2S 3 (0-50 mol % Lu2S3)
    Lomonosov State Academy of Fine Chemical Technology, pr. Vernadskogo 86, Moscow 117571, Russia
    不详
    Russ. J. Inorg. Chem., 2008, 2 (308-312):
  • [7] Phase equilibria at 500 °C of the Mg-Nd-Zn system in the region of 0-50 at %Nd
    Wang, Peisheng
    He, Wei
    Xu, Honghui
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2023, 83
  • [8] Phase equilibria in the Lu-Si-In system at 870 K
    Tyvanchuk, YB
    Zaremba, VI
    Kalychak, YM
    POLISH JOURNAL OF CHEMISTRY, 1998, 72 (05) : 962 - 965
  • [9] PHYSICOCHEMICAL INTERACTION IN THE ALUMINUM PALLADIUM IRON (0-50 AT PERC OF PD) SYSTEM
    FILIPPOVA, AA
    RAEVSKAYA, MV
    SOKOLOVA, IG
    TATARKINA, AL
    VESTNIK MOSKOVSKOGO UNIVERSITETA SERIYA 2 KHIMIYA, 1988, 29 (05): : 530 - 532
  • [10] PHASE EQUILIBRIA IN THE TERNARY Al-Ti-PT SYSTEM. III. THE Al-Ti-PT MELTING DIAGRAM IN THE COMPOSITION RANGE 0-50 at.% PT
    Zaikina, O. V.
    Khoruzhaya, V. G.
    Korniyenko, K. Ye.
    Velikanova, T. Ya.
    POWDER METALLURGY AND METAL CERAMICS, 2019, 58 (1-2) : 81 - 88
12345