Hydrogen storage properties of a Ni, Fe and Ti-added Mg-based alloy

Mg-5wt%Ni-2.5wt%Fe-2.5wt%Ti (referred to as Mg-5Ni-2.5Fe-2.5Ti) hydrogen storage material was prepared by reactive mechanical grinding, after which the hydrogen absorption and desorption kinetics were investigated using a Sievert-type volumetric apparatus. A nanocrystalline Mg-5Ni-2.5Fe-2.5Ti sample was prepared by reactive mechanical grinding and hydriding-dehydriding cycling. Analysis by the Williamson-Hall method from an XRD pattern of this sample after 10 hydriding-dehydriding cycles showed that the crystallite size of Mg was 37.0 nm and that its strain was 0.0407%. The activation of Mg-5Ni-2.5Fe-2.5Ti was completed after three hydriding-dehydriding cycles. The prepared Mg-5Ni-2.5Fe-2.5Ti sample had an effective hydrogen-storage capacity near 5 wt% H. The activated Mg-5Ni-2.5Fe-2.5Ti sample absorbed 4.37 and 4.90 wt% H for 5 and 60 min, respectively, at 593K under 12 bar H2, and desorbed 1.69, 3.81, and 4.85 wt% H for 5, 10 and 60 min, respectively, at 593K under 1.0 bar H2.