Structure and Mechanical Properties of Hot-Pressed Composite Ceramics W2B5–ZrB2–SiC–B4C

被引：0
作者：
D. D. Nesmelov
S. S. Ordan’yan
Yu. P. Udalov
机构：
[1] Saint Petersburg State Institute of Technology (Technical University),
来源：
Refractories and Industrial Ceramics | 2021年 / 62卷
关键词：
ceramics; hot pressing; tungsten boride; zirconium boride; silicon carbide; boron carbide; bending strength; flexural strength; hardness; fracture toughness;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A high-density ceramic material (97% of theoretical density) was obtained by hot pressing of ball-milled powders W2B5, ZrB2, SiC and B4C with holding for 15 minutes at a temperature of 1850°C and a pressure of 30 MPa in an argon atmosphere. The structure and composition of the material were investigated by x-ray diffraction, scanning electron microscopy, and energy-dispersive x-ray spectroscopy. Vickers hardness (19.3 GPa), crack resistance coefficient (5,7 MPa∙m1/2) and bending strength (695 MPa) were determined.
引用
收藏
页码：202 / 207
页数：5
相关论文
共 106 条
[1]  
Ordanyan SS(2014)Nonoxide high-melting point compounds as materials for extreme conditions Adv. Sci. Tech. 89 47-56
[2]  
Vikhman SV(2017)Revisiting the structure of SiC– B Russ. J. Non-Ferr. Met. 58 545-551
[3]  
Nesmelov DD(2009)C– Scripta Mater. 60 559-562
[4]  
Ordanyan SS(2008)B J. Am. Ceram. Soc. 91 26-32
[5]  
Nesmelov DD(2019) systems and prospects for the development of composite ceramic materials based on them J. Alloys Compd. 805 725-732
[6]  
Danilovich DP(2011)Pressureless sintering of ZrB J. Am. Ceram. Soc. 94 4410-4418
[7]  
Udalov YP(2007)–SiC ceramics: the effect of B J. Alloys Compds. 428 197-205
[8]  
Zhang H(2004)C content Adv. Eng. Mater. 6 331-336
[9]  
Yan Y(2010)Pressureless sintering of ZrB Ceram. Int. 36 937-941
[10]  
Huang Z(2019)-SiC ceramics J. Alloy Compd. 785 958-964
12345678910