Nondestructive microstructure analysis of the carbonation evolution process in hardened binder paste containing blast-furnace slag by X-ray CT

被引：0
作者：
Jiande Han
Wei Sun
Ganghua Pan
机构：
[1] Nanjing University of Technology,College of Civil Engineering
[2] Southeast University,School of Materials Science and Engineering
[3] Jiangsu Key Laboratory of Construction Material,undefined
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2013年 / 28卷
关键词：
XCT; hardened binder paste; blast furnace slag; carbonation; gray values; pore structure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We used micro-XCT(X-ray computed tomography) to in-situ investigate the microstructure evolution of hardened binder paste containing different contents (0%, 30%, 50% and 70%) of blast-furnace slag at different carbonation time (0, 3, 7 and 14 days), respectively. The carbonation front shape, the degrees of carbonation and cracks spatial distribution were studied for hardened binder paste containing BFS. In addition, the porosity and pore volume distribution of macro-pore were measured at different carbonation ages. The results reveal that the degree of carbonation at different times can be measured by the volume fraction of the uncarbonated and carbonated parts.
引用
收藏
页码：955 / 962
页数：7
相关论文
共 42 条
[1]  
Zhang X(2004)Carbonation Property of Hardened Binder Pastes Containing Super-Pulverized Blast-Furnace Slag[J] Cement and Concrete Composites 26 371-374
[2]  
Wu K(2009)Modelling of Carbonation of PC and Blended Cement Concrete[J] The IES Journal Part A: Civil & Structural Engineering 2 59-67
[3]  
Yan A(2007)3D Experimental Investigation of the Microstructure of the Cement Pastes Using Synchrotron X-Ray Microtomography (μCT) [J] Cement and Concrete Research 37 360-368
[4]  
Bahador S D(2008)Characterizing the 3D Pore Structure of Hardened Cement Paste with Synchrotron Microtomography [J] Journal of Advanced Concrete Technology 6 273-286
[5]  
Cahyadi J H(2003)Application of X-Ray Computed Tomography to Characterise the Early Hydration of Calcium Aluminate Cement [J] Cement and Concrete Composites 25 145-152
[6]  
Gallucci E(2002)The Visible Cement Data Set [J] Journal of Research of the National Institute of Standards and Technology 107 137-148
[7]  
Scrivener K(2006)X-Ray Microtomography: Application to Microstructure Analysis of A Cementitious Material During Leaching Process [J] Cement and Concrete Research 36 346-357
[8]  
Groso A(2010)Application of Synchrotron Microtomography for Pore Structure Characterization of Deteriorated Cementitious Materials Due to Leaching [J] Cement and Concrete Research 40 1 265-1 270
[9]  
Promentilla M A B(2002)X-Ray Microtomography (MicroCT) of the Progression of Sulfate Attack of Cement Paste [J] Cement and Concrete Research 32 1 673-1 675
[10]  
Sugiyama T(2012)Computational Investigation on Mass Diffusivity in Portland Cement Paste Based on X-Ray Computed Microtomography [J] Construction and Building Materials 27 472-481
12345