Development and investigation on PMMA–PVC blend-based solid polymer electrolytes with LiTFSI as dopant salt

被引：0
作者：
S. Ramesh
Chiam-Wen Liew
机构：
[1] University of Malaya,Centre for Ionics University Malaya, Department of Physics, Faculty of Science
来源：
Polymer Bulletin | 2013年 / 70卷
关键词：
Polymers; Differential scanning calorimetry (DSC); Thermogravimetric analysis (TGA); X-ray diffraction; Electrical conductivity;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
PMMA–PVC polymer blend systems with LiTFSI as dopant salt were prepared by solution casting technique. Studies were then performed to explore the ionic conductivity, crystallographic structure, morphology, and thermal properties of these polymer electrolytes. XRD and SEM reveal amorphous behavior and morphologies of polymer electrolytes, respectively. Coherent length was calculated to determine the amorphousity of polymer complexes. Ionic conductivity was calculated using ac-impedance spectroscopy. DSC measurements revealed a decrease in Tg, whereas Tm and Td were enhanced. The thermal properties of polymer electrolytes were found to enhance upon addition of 30 wt% LiTFSI. Increase in thermal stability of polymer electrolytes were further confirmed through TGA studies.
引用
收藏
页码：1277 / 1288
页数：11
相关论文
共 77 条
  • [1] Xu JJ(2005)undefined Electrochem Commun 7 829-835
  • [2] Ye Hui(2004)undefined Mater Lett 58 641-649
  • [3] Rajendran S(2004)undefined Electrochim Acta 49 2581-2589
  • [4] Sivakumar M(2008)undefined Phys B 403 509-516
  • [5] Subadevi R(2002)undefined Solid State Ionics 148 467-473
  • [6] Saikia D(2008)undefined J Power Sources 180 880-883
  • [7] Kumar A(2007)undefined Eur Polym J 43 4466-4473
  • [8] Rajendran S(2006)undefined Mater Chem Phys 97 330-336
  • [9] Sivakumar P(2009)undefined Curr Appl Phys 9 1106-1111
  • [10] Stephan AM(2007)undefined J Phys Chem Solids 68 407-412
12345678