Impact of Pb substitution on the formation of high Tc superconducting phase in BSCCO system derived through sol-gel process

Sol-gel process was employed to synthesize the Pb-BSCCO system having general composition Bi2−xPbxSr2Ca2Cu3O10−δ, where x=0.2, 0.4 and 0.8. Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), dilatometry and vibrating sample magnetometer (VSM) were employed to study the materials produced at different stages. Two-stage heating firstly at 300 and then 800°C was adopted in order to avoid the burning of the materials and formation of carbonates. The carbonate formation was avoided by heating the materials firstly at 300°C for 2 h and without intermediate cooling moved to the furnace having temperature 800°C and hold for 2 h. The sintering behaviour of samples was studied by dilatometry and the results revealed that the sample having x=0.4 was stabled up to a temperature of 700°C while samples having x=0.2 and 0.8 to a temperature of 625°C. The maximum shrinkage was observed at 850°C in all the samples. On the basis of dilatometry results, the samples were sintered at 845°C for 60 h to observe the superconducting phases. The highest volume fraction of high superconducting phase (2223) was noticed in the sample containing x=0.4 having onset Tc=110 K.