Effect of Heat Treatment on Corrosion, Fatigue, and Corrosion Fatigue Behavior of 17-4PH Stainless Steel

被引：0
|
作者：
M. Ghasemian Malakshah
A. Eslami
F. Ashrafizadeh
A. Berenjkoub
机构：
[1] Isfahan University of Technology,Department of Materials Engineering
来源：
Journal of Materials Engineering and Performance | 2023年 / 32卷
关键词：
17-4PH stainless steel; corrosion; corrosion fatigue; fatigue; heat treatment;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This study investigates effect of heat treatment on fatigue and corrosion fatigue resistance of 17-4PH stainless steel at two thermal cycles, which consisted of 30 min solution annealing at 1050 C and 240 min ageing at 620 C as an overaged thermal cycle, and heat treatment at 464 C for 129 min as an optimized aged thermal cycle. Microstructural characteristics, tensile and hardness properties, corrosion performance, Hydrogen permeation, fatigue and corrosion fatigue resistance of these samples were then compared. Results showed that corrosion resistance and fatigue resistance of aged 17-4PH stainless steel was superior. Despite this, the corrosion fatigue resistance of the heat-treated steels was a function of applied loads and their exposure time to the corrosive environment. In fact, for the lower applied loads/longer exposure times, the overaged steel with higher corrosion rate, and less susceptibility to hydrogen damage had better corrosion fatigue performance, than the aged 17-4PH stainless steel.
引用
收藏
页码：6610 / 6621
页数：11
相关论文
共 50 条
  • [1] Effect of Heat Treatment on Corrosion, Fatigue, and Corrosion Fatigue Behavior of 17-4PH Stainless Steel
    Malakshah, M. Ghasemian
    Eslami, A.
    Ashrafizadeh, F.
    Berenjkoub, A.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (15) : 6610 - 6621
  • [2] Effect of Aging Heat Treatment on Corrosion Behavior and Corrosion Kinetics of 17-4PH Stainless Steel in Artificial Saliva
    Kosasang, Onthida
    Wongkaewmoon, Manutchaya
    Chumphongphan, Somwan
    SAINS MALAYSIANA, 2021, 50 (03): : 849 - 858
  • [3] Corrosion fatigue behavior of 17-4 PH stainless steel in different tempers
    Lin, CK
    Lin, CP
    FATIGUE AND FRACTURE MECHANICS: 33RD VOLUME, 2003, 1417 : 598 - 613
  • [4] Effect of aging heat treatment on microbiologically influenced corrosion of 17-4PH stainless steel by Pseudomonas aeruginosa
    Zhao, Li
    Qian, Hongchang
    Chang, Weiwei
    Guo, Dawei
    Kwok, Chi Tat
    Tam, Lap Mou
    Zhang, Dawei
    CORROSION SCIENCE, 2024, 227
  • [5] Inhibitive Effect of Nitrate on Pitting Corrosion of 17-4PH Stainless Steel
    Seyedi, M.
    Mirjalili, M.
    Taji, I.
    Armat, O.
    Moayed, M. H.
    CORROSION, 2017, 73 (02) : 181 - 191
  • [6] Effect of different heat-treatment processes on corrosion resistance of 17-4PH steel
    Chen, Xiaoqin
    Qin, Xiaofei
    Li, Yue
    Cheng, Wenjia
    Jin, Haonan
    Li, Quan
    BULLETIN OF MATERIALS SCIENCE, 2024, 47 (04)
  • [7] Pitting corrosion behavior of friction-surfaced 17-4PH stainless steel coatings with and without subsequent heat treatment
    Guo, D.
    Chen, J.
    Chen, X.
    Shi, Q.
    Cristino, V. A. M.
    Kwok, C. T.
    Tam, L. M.
    Qian, H.
    Zhang, D.
    Li, X.
    CORROSION SCIENCE, 2021, 193
  • [8] Effect of hydrostatic pressure on the pitting corrosion of 17-4PH martensitic stainless steel
    Ma, Hongyu
    Liu, Rui
    Ke, Peiling
    Cui, Yu
    Liu, Li
    Wang, Fuhui
    ENGINEERING FAILURE ANALYSIS, 2022, 138
  • [9] The influence of corrosion pits on the fatigue life of 17-4PH steam turbine blade steel
    Schoenbauer, Bernd M.
    Stanzl-Tschegg, Stefanie E.
    Perlega, Andrea
    Salzman, Ronald N.
    Rieger, Neville F.
    Turnbull, Alan
    Zhou, Shengqi
    Lukaszewicz, Mikolaj
    Gandy, David
    ENGINEERING FRACTURE MECHANICS, 2015, 147 : 158 - 175
  • [10] EFFECT OF HEAT-TREATMENT ON CORROSION-FATIGUE CRACK GROWTH IN 17-4 PH STEEL
    CROOKER, TW
    CARES, WR
    REPORT OF NRL PROGRESS, 1974, (MAR): : 39 - 41
12345