A comparative study on the processing, dielectric and electrical properties of PMN based solid solutions

被引：0
作者：
Kamal Singh
Sheela Band
机构：
[1] Amravati University,Department of Physics
[2] Y. C. Engineering College,Department of Applied Physics
来源：
Bulletin of Materials Science | 1997年 / 20卷
关键词：
Solid solution; sintering; relaxor; microstructure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Lead magnesium niobate (PMN) based binary with lead titanate (PT), lead iron niobate (PFN) and lead zinc niobate (PZN) and ternary with PZN-PT and PFN-PT solid solutions have been synthesized. In depth characterization using X-ray diffraction and SEM techniques have revealed the major perovskite phase formation. Amongst all the solid solutions, PMN-PZN-PT has given the highest values of permittivity as 19,740 and 23,700 withTc as 34°C when sintered at 1080°C and 1180°C respectively on the one hand and on the other, PFN containing solid solutions exhibited distinct deviation from the relaxor behaviour.
引用
收藏
页码：265 / 277
页数：12
相关论文
共 38 条
[1]  
Bokov V A(1961)undefined Sov. Phys. Solid State 2 2428-2428
[2]  
Mylnikova I E(1991)undefined J. Am. Ceram. Soc. 74 1152-1152
[3]  
Bouquin O(1983)undefined Mater. Chem. & Phys. 8 469-469
[4]  
Lejeune M(1994)undefined J. Appl. Phys. 33 5423-5423
[5]  
Desgardin G(1990)undefined J. Am. Ceram. Soc. 73 913-913
[6]  
Bali H(1985)undefined Mater. Res. Bull. 20 493-493
[7]  
Raveau B(1991)undefined J. Am. Ceram. Soc. 74 2996-2996
[8]  
Ichionse K(1987)undefined Am. Ceram. Soc. Bull. 66 704-704
[9]  
Kato N(1996)undefined Ferroelectrics 175 193-193
[10]  
Landin S M(1959)undefined Sov. Phys. Solid State 1 1429-1429
1234