Studies on syntheses and dynamic swelling of pH-sensitive macroporous poly(N-isopropylacrylamide-co-acrylic acid) hydrogels

A series of macroporous poly(N-isopropylacrylamide-co-acrylic acid) (PNIPAm-AA) hydrogels with different composition were synthesized by free-radical copolymerization in the presence of silica particles as a pore generating agent. The equilibrium swelling ratio, half swelling time and dynamic swelling kinetics of the copolymers previously soaked in different acidic buffer solutions were investigated at pH 7 at 25°C. Experimental results revealed that the swelling rate of the macroporous hydrogels was greatly increased compared to conventional hydrogels due to existence of the macroporous structures. It was found that the swelling history of previously putting in acidic solutions copolymers had strong influence on their dynamic swelling kinetics especially for the samples ranging in composition between 30 and 70 mol % of NIPAAm, whereas the swelling history had little influence on the equilibrium swelling ratio of copolymers. The swelling pattern exhibits sigmoid swelling curves. This is explained by an autocatalytic mechanism. The hydrogen bonding dissociation plays an important role in the dynamic swelling behavior.