X-ray residual stress measurement on mechanical components with high curvature

被引：8

作者：

T. Berruti

M. M. Gola

机构：

[1] Department of Mechanical Engineering, Politecnico di Torino, Torino 10129, Corso Duca degli Abruzzi

来源：

Experimental Mechanics | 2003年 / 43卷 / 1期

关键词：

Curvature; Loading devices; Measurement area; Residual stress; X-ray diffraction;

D O I：

10.1007/BF02410491

中图分类号：

学科分类号：

摘要：

In this paper we deal with the definition of an appropriate X-ray diffraction procedure for residual stress determination on samples with high curvature radius. We choose as the application high-strength hot worked coil springs for car suspensions (wire diameter d = 12 mm). Different methods of X-ray measurement area limitation are compared, taking into account the measurement errors, for the determination of stress in one and in three directions. After the identification of the irradiated area limits for plane samples, further limits are identified due to the sample curvature (torsion bar). We describe loading devices purposely designed, constructed and calibrated. In each case, the sample is loaded so that the stress state is determined at the same time both by strain gages and by X-ray measurement.

引用

页码：105 / 114

页数：9

共 16 条

[1]

Zantopulos H., Jatczac C.F., Systematic errors in X-ray diffractometer stress measurements due to specimen geometry and beam divergence, Advances in X-Ray Analysis, 14, pp. 360-376, (1970)

[2]

Jo J., Hendricks R.W., Diffractometer misalignment errors in X-ray residual stress measurements, J. Appl. Cryst., 24, pp. 878-887, (1991)

[3]

Convert F., Miege B., The control of geometrical sources of error in X-ray diffraction applied to stress analysis, J. Appl. Cryst., 25, pp. 384-390, (1992)

[4]

Francois M., Dionnet B., Sprauel J.M., Nardou F., The influence of cylindrical geometry on X-ray stress tensor analysis. I. General formulation, J. Appl. Cryst., 28, pp. 761-767, (1992)

[5]

Dionnet B., Francois M., Lebrun J.L., Nardou F., Influence of tore geometry on X-ray stress analysis, Proc. 4th Eur. Conf. on Residual Stresses, pp. 327-336, (1996)

[6]

Guillen R., Cossu C., Jacquot T., Francois M., Bourniquel B., X-ray diffraction texture analysis of cylindrical samples, J. Appl. Cryst., 32, pp. 387-392, (1999)

[7]

Méthods D'essais Pour L'analyse des Contraintes Résuduelles Par Diffraction Des Rayons X, (1999)

[8]

Residual stress measurement by X-ray diffraction, SAE J784a, (1971)

[9]

Standard test method for determining the effective elastic parameter for x-ray diffraction measurements of residual stress, ASTM E1426-94

[10]

ASM Handbook, Residual Stress Measurements, Mechanical Testing and Evaluation, 8, (2000)

← 1 2 →