Tribological Properties of Surface Friction Hardened AISI 316L Steel

被引：2
|
作者：
Khaksaran, A. [1 ]
Taghiabadi, R. [1 ]
Jafarzadegan, M. [1 ]
机构：
[1] Imam Khomeini Int Univ, Dept Mat Sci, Qazvin, Iran
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2021年 / 74卷 / 08期
关键词：
AISI; 316L; Friction hardening; Hardness; Tribology; Friction; wear;
D O I：
10.1007/s12666-021-02306-6
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Friction hardening was employed to improve the tribological properties of AISI 316L austenitic stainless steel (ASS 316L). The process was conducted using a hard indenter (74 +/- 1 HRC) under the travel speeds of 90, 180, and 360 mm/s for 30 and 60 passes. The results showed that FH increased the surface hardness of annealed ASS 316L alloy by 180%. The sliding wear tests also showed the positive impact of FH on the wear resistance and friction behaviour. For instance, at the applied pressure of 1 MPa, the wear rate and coefficient of friction (COF) of FHed ASS 316L sample (90 mm/s, 30 passes) were reduced by 68 and 20%, respectively, as compared to those of the annealed sample.
引用
收藏
页码：1979 / 1989
页数：11
相关论文
共 50 条
  • [1] Tribological Properties of Surface Friction Hardened AISI 316L Steel
    A. Khaksaran
    R. Taghiabadi
    M. Jafarzadegan
    Transactions of the Indian Institute of Metals, 2021, 74 : 1979 - 1989
  • [2] Tribological Properties of AISI 316L Steel Surface Layer Implanted with Rare Earth Element
    Sartowska, B.
    Barlak, M.
    Walis, L.
    Starosta, W.
    Senatorski, J.
    Kosinska, A.
    ACTA PHYSICA POLONICA A, 2015, 128 (05) : 923 - 926
  • [3] Properties of the Passive Film Formed on Interstitially Hardened AISI 316L Stainless Steel
    Niu, W.
    Lillard, R. S.
    Li, Z.
    Ernst, F.
    ELECTROCHIMICA ACTA, 2015, 176 : 410 - 419
  • [4] Study of boriding surface treatment in the tribological behavior of an AISI 316L stainless steel
    Arteaga-Hernandez, L.A.
    Cuao-Moreu, C.A.
    Gonzalez-Rivera, C.E.
    Alvarez-Vera, M.
    Ortega-Saenz, J.A.
    Hernandez-Rodriguez, M.A.L.
    Wear, 2021, 477
  • [5] Study of boriding surface treatment in the tribological behavior of an AISI 316L stainless steel
    Arteaga-Hernandez, L. A.
    Cuao-Moreu, C. A.
    Gonzalez-Rivera, C. E.
    Alvarez-Vera, M.
    Ortega-Saenz, J. A.
    Hernandez-Rodriguez, M. A. L.
    WEAR, 2021, 477
  • [6] Duplex surface treatment of an AISI 316L stainless steel; microstructure and tribological behaviour
    Heras, E. De Las
    Egidi, D. A.
    Corengia, P.
    Gonzalez-Santamaria, D.
    Garcia-Luis, A.
    Brizuela, M.
    Lopez, G. A.
    Martinez, M. Flores
    SURFACE & COATINGS TECHNOLOGY, 2008, 202 (13): : 2945 - 2954
  • [7] Tribological and adhesion properties of microwave-assisted borided AISI 316L steel
    Ipek Ayvaz, Safiye
    Aydin, Ibrahim
    MATERIALS TESTING, 2022, 64 (02) : 249 - 259
  • [8] Linear friction welding of AISI 316L stainless steel
    Bhamji, Imran
    Preuss, Michael
    Threadgill, Philip L.
    Moat, Richard J.
    Addison, Adrian C.
    Peel, Matthew J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 528 (02): : 680 - 690
  • [9] Tribological properties of titanium surface alloyed 316L stainless steel
    Liu, Weiyan
    Li, Xiuyan
    Wang, Hefeng
    Feng, Rui
    Tang, Bin
    MANUFACTURING PROCESSES AND SYSTEMS, PTS 1-2, 2011, 148-149 : 740 - +
  • [10] Evaluation of the tribological performance of the green hBN nanofluid on the friction characteristics of AISI 316L stainless steel
    Akincioglu, Sitki
    Sirin, Senol
    INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2021, 73 (09) : 1176 - 1186
12345