New manufacturing process of nickel-free austenitic stainless steel with nitrogen absorption treatment

被引:28
作者
Kuroda, D [1 ]
Hanawa, T
Hibaru, T
Kuroda, S
Kobayashi, M
Kobayashi, T
机构
[1] Natl Inst Mat Sci, Ctr Biomat, Tsukuba, Ibaraki 3050047, Japan
[2] Natl Inst Mat Sci, Steel Res Ctr, Tsukuba, Ibaraki 3050047, Japan
[3] Natl Inst Mat Sci, Mat Anal Stn, Tsukuba, Ibaraki 3050047, Japan
关键词
nickel-free austenitic stainless steel; nitrogen absorption; mechanical properties; microstructure; manufacturing process;
D O I
10.2320/matertrans.44.414
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Ingots of ferritic stainless steels, Fe-24Cr and Fe-24Cr-2Mo in mass%, were worked to various dimensions for test specimens. Nitrogen was absorbed by the specimens in a furnace filled with nitrogen gas with a pressure of 101.3 kPa at 1473 K to develop a simple and convenient manufacturing process of nickel-free austenitic stainless steels. Changes in the mechanical properties of the alloys with nitrogen absorption treatment are discussed on the basis of the resultant microstructure. Ferritic Fe-24Cr and Fe-24Cr-2Mo were austenitized with nitrogen absorption to a 2-mm depth from the surface. The hardness, tensile strength, 0.2% proof stress, and elongation to fracture increased, and the reduction of area decreased in Fe-24Cr and Fe-24Cr-2Mo by austenitization due to nitrogen absorption. The tensile strength and 0.2% proof stress of these alloys with nitrogen absorption for 129.6 ks were much larger than those of 316L steel, while the elongation to fracture was much smaller than that of 316L steel. Therefore, small devices and parts with a maximum thickness or diameter of 4 mm were manufactured with this process in this study.
引用
收藏
页码:414 / 420
页数:7
相关论文
共 31 条
[1]  
AHMEDZAID S, 1989, P INT C HIGH NITR ST, P240
[2]  
CHANG LW, 1996, TOXICOLOGY METALS, P827
[3]  
DEGALLAIX S, 1986, MATER SCI TECH SER, V2, P946, DOI 10.1179/026708386790219624
[4]  
Endo K., 1998, ZAIRYO TOKANKYO, V47, P570
[5]  
FORCH K, 1992, STAHL EISEN, V112, P53
[6]  
Gebeau RC, 2001, ADV MATER PROCESS, V159, P46
[7]  
GUEVEL PL, 1989, P INT C HIGH NITR ST, P245
[8]   A THERMODYNAMIC ANALYSIS OF THE FE-CR-N SYSTEM [J].
HERTZMAN, S ;
JARL, M .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (10) :1745-1752
[9]  
*IARC WORK GROUP E, 1999, IARC MON EV CARC RIS, V74, P241
[10]  
*JAP STAINL STEEL, 1995, SUT BINR, P491