Influence of grain refinement on hot tearing in B206 and A319 aluminum alloys

Aluminum-copper (Al-Cu) and aluminum-silicon-copper (Al-Si-Cu) alloys are among the most common aluminum casting alloys. Aluminum alloy B206 is a relatively new Al-Cu alloy with high strength and ductility at room and elevated temperatures, while A319 is an Al-Si-Cu alloy with good strength and excellent wear resistance. However, despite their advantages, when these alloys are cast via the permanent mold casting (PMC) process, they show a high susceptibility to hot tearing. Grain refinement has shown promise as a means to reducing hot tears in aluminum alloys. In this study, Ti-B grain refiner was used to investigate the effect of grain refinement on hot tearing in B206 and A319 aluminum alloys during permanent mold casting. The results suggest that Ti-B additions significantly reduced hot tearing in B206 and A319. Grain sizes were also seen to reduce significantly in both alloys with addition of Ti-B grain refiner. However, Ti-B grain refiner had a diverse effect on alloy grain morphology, as a dendritic morphology in B206 was transformed to a more globular one, while in A319, the grain structure remained dendritic.