Evaporation of Cr2O3 in atmospheres containing H2O

被引：78

作者：

Yamauchi, A ^{[1
]}

Kurokawa, K ^{[1
]}

Takahashi, H ^{[1
]}

机构：

[1] Hokkaido Univ, Grad Sch Engn, Div Mol Chem, Sapporo, Hokkaido 0608628, Japan

来源：

OXIDATION OF METALS | 2003年 / 59卷 / 5-6期

关键词：

high-temperature oxidation; H2O-containing atmosphere; evaporation of Cr2O3; deterioration of Cr2O3 scale;

D O I：

10.1023/A:1023671206976

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Stainless steels in atmospheres containing H2O form a Cr2O3 scale in the early stage of oxidation. However, the Cr2O3 scale gradually degrades with time. In order to determine the effect of H2O on the deterioration of a Cr2O3 scale, the evaporation behavior of Cr2O3 in N-2-O-2-H2O atmospheres was investigated. The rate of mass loss in an N-2-O-2-H2O atmosphere was found to be one order of magnitude higher than the rates in N-2-O-2 and N-2-H2O atmospheres, indicating that deterioration of the Cr2O3 scale is likely to occur in mixed atmospheres of oxygen and water vapor. Volatilization of Cr2O3 is probably based on the following reactions: 1/2 Cr2O3(s) + 3/4 O-2(g) + H2O(g) GCrO(2)(OH)(2)(g). However, it is also speculated that the reaction, Cr2O3(s) + 3/2 O-2(g) = 2CrO(3)(g), affects the evaporation of Cr2O3 at temperatures higher than 1323 K. The evaporation rate of Cr2O3 is roughly comparable to the growth rate of the Cr2O3 scale. Therefore, a Cr2O3 scale can be degraded by the evaporation of Cr2O3.

引用

页码：517 / 527

页数：11

共 50 条

[21] Oxidation Behaviour of Sanicro 25 (42Fe22Cr25NiWCuNbN) in O2/H2O Mixture at 600 °C [J].

Intiso, L. ;

Johansson, L. -G. ;

Canovic, S. ;

Bellini, S. ;

Svensson, J. -E. ;

Halvarsson, M. .

OXIDATION OF METALS, 2012, 77 (5-6) :209-235

[22] Low cost rare earth elements deposition method for enhancing the oxidation resistance at high temperature of Cr2O3 and Al2O3 forming alloys [J].

Paúl, A ;

Elmrabet, S ;

Odriozola, JA .

JOURNAL OF ALLOYS AND COMPOUNDS, 2001, 323 :70-73

[23] Modelling Cr depletion under a growing Cr2O3 layer on austenitic stainless steel: the influence of grain boundary diffusion [J].

Hansson, Anette N. ;

Hattel, Jesper H. ;

Dahl, Kristian V. ;

Somers, Marcel A. J. .

MODELLING AND SIMULATION IN MATERIALS SCIENCE AND ENGINEERING, 2009, 17 (03)

[24] Oxidation of Fe-Si alloys in CO2-H2O atmospheres [J].

Li, Huan ;

Zhang, Jianqiang ;

Young, David J. .

MATERIALS AT HIGH TEMPERATURES, 2011, 28 (04) :297-301

[25] Stress release in α-Cr2O3 oxide thin films formed on Ni30-Cr and Fe47-Cr alloys [J].

Guerain, M. ;

Rakotovao, F. ;

Brou, S. Y. ;

Bonnet, G. ;

Panicaud, B. ;

Grosseau-Poussard, J. L. ;

Goudeau, P. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 718 :223-230

[26] Oxidation Properties of Metal/Ceramic Interconnectors for SOFC's in Air, Ar-H2-H2O and Ar-CH4-H2O Atmospheres [J].

Prybylski, Kazimierz .

HIGH-TEMPERATURE OXIDATION AND CORROSION 2010, 2011, 696 :400-405

[27] Formation of protective Cr2O3 scale at high temperature and the effect of mass transport in the presence of water vapor [J].

Bin Ani, Mohd Hanafi ;

Othman, Raihan .

ADVANCES IN METALLURGICAL AND MINING ENGINEERING, 2012, 402 :412-420

[28] Raman microprobe spectroscopy measurements of residual stress distribution along blisters in Cr2O3 thin films [J].

Kemdehoundja, M. ;

Grosseau-Poussard, J. L. ;

Dinhut, J. F. .

APPLIED SURFACE SCIENCE, 2010, 256 (09) :2719-2725

[29] In situ growth-stress measurement of Cr2O3 scale formed on stainless steels by Raman spectroscopy [J].

Kitamura, K. ;

Nishiyama, Y. ;

Otsuka, N. ;

Kudo, T. .

HIGH-TEMPERATURE OXIDATION AND CORROSION 2005, 2006, 522-523 :489-495

[30] Oxidation of Fe-10Cr in O2 and in O2+H2O environment at 600 °C: A microstructural investigation [J].

Jonsson, T. ;

Pujilaksono, B. ;

Heidari, H. ;

Liu, F. ;

Svensson, J. -E. ;

Halvarsson, M. ;

Johansson, L-G. .

CORROSION SCIENCE, 2013, 75 :326-336

← 1 2 3 4 5 →