Evaporation of Cr2O3 in atmospheres containing H2O

被引：78
作者：
Yamauchi, A [1 ]
Kurokawa, K [1 ]
Takahashi, H [1 ]
机构：
[1] Hokkaido Univ, Grad Sch Engn, Div Mol Chem, Sapporo, Hokkaido 0608628, Japan
来源：
OXIDATION OF METALS | 2003年 / 59卷 / 5-6期
关键词：
high-temperature oxidation; H2O-containing atmosphere; evaporation of Cr2O3; deterioration of Cr2O3 scale;
D O I：
10.1023/A:1023671206976
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Stainless steels in atmospheres containing H2O form a Cr2O3 scale in the early stage of oxidation. However, the Cr2O3 scale gradually degrades with time. In order to determine the effect of H2O on the deterioration of a Cr2O3 scale, the evaporation behavior of Cr2O3 in N-2-O-2-H2O atmospheres was investigated. The rate of mass loss in an N-2-O-2-H2O atmosphere was found to be one order of magnitude higher than the rates in N-2-O-2 and N-2-H2O atmospheres, indicating that deterioration of the Cr2O3 scale is likely to occur in mixed atmospheres of oxygen and water vapor. Volatilization of Cr2O3 is probably based on the following reactions: 1/2 Cr2O3(s) + 3/4 O-2(g) + H2O(g) GCrO(2)(OH)(2)(g). However, it is also speculated that the reaction, Cr2O3(s) + 3/2 O-2(g) = 2CrO(3)(g), affects the evaporation of Cr2O3 at temperatures higher than 1323 K. The evaporation rate of Cr2O3 is roughly comparable to the growth rate of the Cr2O3 scale. Therefore, a Cr2O3 scale can be degraded by the evaporation of Cr2O3.
引用
收藏
页码：517 / 527
页数：11
相关论文
共 50 条
[11]   Development of a modified CVD coating process for the enhancement of the high temperature oxidation resistance of Cr2O3 and Al2O3 forming alloys [J].
Paúl, P ;
Odriozola, JA .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 300 (1-2) :22-33
[12]   Oxygen Permeability Measurements in Ni Using H2/H2O, CO/CO2 and Ni/NiO Rhines Pack Atmospheres [J].
Guo, Pingyi ;
Zhang, Jianqiang ;
Young, David J. ;
Konrad, Christian H. .
OXIDATION OF METALS, 2015, 83 (3-4) :223-235
[13]   Oxidation of Binary FeCr Alloys (Fe-2.25Cr, Fe-10Cr, Fe-18Cr and Fe-25Cr) in O2 and in O2 + H2O Environment at 600 °C [J].
Pujilaksono, B. ;
Jonsson, T. ;
Heidari, H. ;
Halvarsson, M. ;
Svensson, J. -E. ;
Johansson, L. -G. .
OXIDATION OF METALS, 2011, 75 (3-4) :183-207
[14]   Improved Cr2O3 adhesion by Ce ion implantation in the presence of interfacial sulfur segregation [J].
Li, M. S. ;
Hou, P. Y. .
ACTA MATERIALIA, 2007, 55 (02) :443-453
[15]   Effect of water vapour partial pressure on the chromia (Cr2O3)-based scale stability [J].
Mahboubi, Shooka ;
Zurob, Hatem S. ;
Botton, Gianluigi A. ;
Kish, Joey R. .
CANADIAN METALLURGICAL QUARTERLY, 2018, 57 (01) :89-98
[16]   Corrosion Resistance of Cr2O3, ZrO2, and Mn3O4 Oxide Films to Lead-Bismuth Eutectic: A Comparative Study [J].
Liu, Tao ;
Liu, Wenguan ;
Yang, Chongdou ;
Lei, Penghui ;
Yun, Di ;
Qiu, Jie .
MATERIALS, 2024, 17 (23)
[17]   ReaxFF reactive molecular dynamics study on oxidation behavior of 3C-SiC in H2O and O2 [J].
Chen, Zhuangzhuang ;
Sun, Zhigang ;
Chen, Xihui ;
Wu, Youxun ;
Niu, Xuming ;
Song, Yingdong .
COMPUTATIONAL MATERIALS SCIENCE, 2021, 195
[18]   Oxidation of FeCrAl foils at 500-900°C in dry O2 and O2 with 40% H2O [J].
Engkvist, J. ;
Canovic, S. ;
Liu, F. ;
Gotlind, H. ;
Svensson, J. -E. ;
Johansson, L. -G. ;
Olsson, M. ;
Halvarsson, M. .
MATERIALS AT HIGH TEMPERATURES, 2009, 26 (02) :199-210
[19]   Study on Local Residual Stress in a Nanocrystalline Cr2O3 Coating by Micro-Raman Spectroscopy [J].
Li, Qiu ;
Gou, Yanrong ;
Wang, Tie-Gang ;
Gu, Tingyi ;
Yu, Qiang ;
Wang, Lijie .
COATINGS, 2019, 9 (08)
[20]   Characterization of a Cr2O3 scale formed on chromium with implanted yttrium ions by advanced electron microscopy [J].
Gil, A. ;
Kryshtal, O. ;
Brylewski, T. ;
Czyrska-Filemonowicz, A. .
SURFACE & COATINGS TECHNOLOGY, 2019, 368 :232-242
12345